连续感应淬火的轴类零件首尾相连处屏蔽问题地研究.pdfVIP

连续感应淬火的轴类零件首尾相连处屏蔽问题的研究 尤亦凡 杨文俊 (上海工业大学嘉定通用机械有限公司 上海 201822) 摘 要：在卧式轴类感应淬火自动生产线上，采用 0 型感应圈对轴类零件进行感应淬火。通过目视 法分析了轴类零件首尾相连处纵向剖面硬化层的形状。结果表明，轴类零件尾部硬化层呈内八字的 包入状，深度超出要求；而紧连着的后一根轴的头部硬化层呈外八字的后缩状，深度不到要求。这 是由于轴类零件首尾相连处的间隙对 0 型感应圈的磁场产生了屏蔽影响。采用П型感应圈后，可以 基本消除屏蔽影响，使轴类零件首尾相连处的硬化层的形状与其它部位基本一样。 关键词：连续感应淬火；轴类零件；屏蔽；硬化层形状；感应圈 The research of how to avoid magnetic field shielding at the position of end to end in the shaft ‘s continuous Induction Hardening You Yi- fan Yang Wen-jun (Shanghai Industry University Jia Ding General Machinery Co., Ltd Shanghai 201822) Abstract: We use 0-shape coil On the horizontal and continuous type quenching machine to harden shaft, Through the microscope, we analysis the vertical cutting-sample’s harden layer profile of two end of rod. The results show that the fist hardened rod ‘s end are almost through hardened and the case depth exceeds requirements; the next end is un-adequate hardened, and the case depth under the requirements.This is because that the gap between two rod generated a shielding effect to the magnetic field generated by 0-type coil. Using П-type coil can basically eliminate shielding effect, obtain the uniform case depth at the position of end-to-end. Keywords : Continuous induction hardening; Shaft; Shielding; Hardening layer shape; coil 小型轴类零件的外圆面感应淬火，一般采用感应加热电源加立式或卧式带顶尖的轴类淬火机床 进行，也可采用由上下料装置、输送装置、感应加热电源等组成的轴类自动生产线进行。后者的生 产效率比前者生产效率高出许多，因此，只要是上批量的小型轴类零件，特别是没有中心孔的小型 轴类零件，采用轴类自动生产线进行感应淬火成了首选。但小型轴类零件在整个外圆面都需要一定 硬化层深度的情况下，经自动生产线感应淬火的轴类零件头部的硬化层深度达不到技术要求。我厂 在为某客户的滚柱轴实施表面感应淬火过程中就遇到了此类问题。滚柱轴的简图如图 1 所示。滚柱 轴感应淬火的技术要求见表 1。 图1 滚柱轴的简图 表1 滚柱轴感应淬火的技术要求 零件名称 材料 硬化层深度 表面硬度 硬化区范围 Φ8 滚柱轴 60 400HV1=0.8∽1.3 mm 54-