C3000气缸体铸造工艺设计优化及生产控制.pdfVIP

2013 国铸造活动周论文集 C3000 缸体铸造工艺设计优化及生产控制 刘明 ，李小举 1 （广西玉柴机器股份有限公司，广西 玉林 537005 ） 摘要：对C3000 气缸体现有的铸造工艺重新优化，并利用MAGMA 软件对浇注系统进行模拟优化。 通过采用 间档进水的浇注方式，合理布置外模排气针，重新设定现场工艺参数以及生产控制措施， 大大降低了爆砂、缩孔、气孔等缺陷的出现，生产出的铸件质量稳定、可靠，完全能满足用户需求。 关键词：工艺优化；铸造缺陷；生产控制 Technology Optimization of Casting Process Design and Production Control of C3000 Cylinder LIU Ming，LI Xiao-ju （Guangxi Yuchai Machinnery Co., Ltd., Yulin 537005, Guangxi ） Abstract：To reflect some of the casting process to optimize C3000 cylinder, and gating system to make use of MAGMA software simulation optimization. By adopting the intermediate file into the water pouring way, reasonable decorate mold venting needle, reset the field process parameters as well as a series of production control measures, and greatly reduces the sand blasting, shrinkage cavity, porosity, etc. Output of the casting quality is stable, reliable and can fully satisfy customers needs. Key words：technology optimization；casting defects ；production control 2012 年制造业市场持续低迷，整个发动机行 产销量下滑，玉柴也大受影响。但玉柴 6C 系列 船电用发动机却逆势增加，该系列发动机用机体毛坯在玉柴铸造厂生产。自20 11 年试产以来，废品 率居高不下。20 12 年，市场订单不断增加，与此同时，铸件的质量问题也不断暴露出来，爆砂、缩 孔等缺陷不断出现，废品率一度高达 23.89%。经过采用 MAGMA 软件对铸件浇注系统模拟并重新 改进了浇注系统，针对现场实际操作情况对工艺进行重新优化，通过特定的控制要求和措施来指导 现场生产，使得铸件的质量情况得到彻底改观，成功实现C3000 机体的批量产出。质量稳定、可靠 的铸件满足了用户的需要，为公司创造了巨大的经济效益，为以后大型铸件生产提供了非常重要的 技术指导。 1 C3000 机体铸件简介 6C 系列发动机使用C3000 机体毛坯 （如图1）。 作者简介：刘 （1989-），男，助理工程师，主要从事铸造工艺、工装设计等工作。E-mail：sculiuming@163.com。 1 2013 国铸造活动周论文集 图1 C3000 机体毛坯 产品轮廓尺寸为1624mm ×658mm ×865mm，是目前该厂批量生产体积最大、重量最重的机型。 其材质为HT250 ，整台毛坯重量大约为1190kg 。 2 浇注系统优化 2.1 对之前的浇注系统进行模拟分析 采用MAGMA 软件对浇注系统进行模拟，如图2 所示。 图