角钢滚动导卫在安钢400型材机组与应用.pdfVIP

1角钢滚动导卫在安钢 400 型材机组的应用 匡祖国 刘书敏 （安阳钢铁股份有限公司，安阳 457500 ） 摘 要 型钢生产，因轧件断面复杂，多使用滑动导卫装置，滚动导卫使用有较大难度。为提高产品表面质量，安 钢400 型材机组在∠80～∠100 角钢成品入口成功应用滚动导卫装置，告别了400 型机组只能使用滑动导卫的历史。 应用滚动导卫后，成品质量稳定性大为提高，解决了大规格角钢易产生刮痕[1]缺陷的难题，市场上没有接到表面质 量缺陷方面的质量异议。万吨钢检验废由原来的50t降到20t 。起到了较好的质量改进效果。 关键词 刮痕 角钢 质量改进 滚动导卫 应用 Application Of Angle Rolling Guide In φ400mm Section Stands In Angang Group Kuang Zuguo Liu Shumin (Anyang IronSteel Group Co.,Ltd., Anyang, 457500) Abstract During the section steel rolling processes, the simple sliding guide was mainly used due to the pass complex section. The rolling guide was not easily.In order to improve the surface quality, the complicated rolling guide was successfully used for ∠80～∠100 angle steel’s production in the Φ400 section stands , the quality of the finished product was improved greatly. It also resolved the problem of the cupped dent on the surface of large size angle steel. No customer complains about angle steel’s surface defect was received. The weight of waste product per 10 thousand ton reduced from 50 ton to 20 ton. Quality improvement is reached. Key words cupped dent, angle steel, quality improvement, rolling guide, application 1 引言 滚动导卫在棒材连轧机组使用较为普及。棒材轧制，孔型结构简单，轧件变形均匀，滚动导卫的导辊外 形简单，能较稳定的夹持轧件，对提高棒材的轧制效率，减少刮痕等产品表面质量缺陷起到较好作用。型钢 轧制，孔型结构复杂，轧件不均匀变形大，目前仍较多使用滑动导卫装置，由此带来轧制效率低，刮痕等表 面质量缺陷多等问题。为提高轧制效率和产品质量，型钢生产非常有必要推广应用滚动导卫。 2 概况及存在问题 安阳钢铁股份有限公司第一轧钢厂ф400mm 机组是河南省唯一生产复杂断面型材的专业车间，年产量 60 多万吨。主要产品有∠45~∠100 等边角钢、≮63 ×40 、≮75 ×50 不等边角钢、[6.3~[10 槽钢、φ30~ φ 50 中圆钢，其中角钢为ф400mm 型材机组主导产品，约占年产量的80%，角钢生产全部采用滑动导卫，结 构简单。入口导卫为左右导板、下托板、上压盖结构，见图1。靠左右导板，夹持角钢左右两腿，将轧件导 匡祖国（1973—），男，硕士，高工。 角钢滚动导卫在安钢400 型材机组的应用 8-549 进轧槽。在成品入