关于离心轧辊辊身亮斑问题探讨.pdfVIP

关于离心轧辊辊身亮斑问题的探讨 刘 娜 艾忠诚 李 琳 李艳红 张福海 （鞍钢重型机械有限责任公司轧辊厂，鞍山 114021 ） 1 摘 要 在离心轧辊生产时，个别轧辊工作层存在成分偏析。这表现为工作层表面碳化物聚集的亮斑缺陷，且工作 层内部呈不规则层状分布。本文通过对问题轧辊的缺陷部位的硬度、化学成分和金相的检测，对亮斑产生的原因进 行分析，确定了成分不均、孕育问题、铁水紊流和离心机振动是造成轧辊亮斑问题的主要原因。 关键词 离心轧辊 成分偏析 碳化物 孕育 紊流 The Research of Irregular Speck on Barrel of Centrifugate Roll Liu Na Ai Zhongcheng Li Lin Li Yanhong Zhang Fuhai (Roll Works of Angang Heavy Machinery Corporation, Ltd., Anshan, 114021 ) Abstract The work coating of centrifugate roll occasionally occurs segregation of component ,which displays that carbide aggregates to form defects of irregular peck on the surface of the work coating, the carbide distributes Irregularly and lamellar. This article analyse reasons of irregular speck forming , thinks they are prime reasons that are uneven component ,inoculation,turbulent and vibration of centrifuger, through detecting hardness, component and metallic phase in the defect roll. Key words centrifugate roll, segregation of component , carbide ,inoculation,turbulent 在轧辊生产过程中，铸造缺陷常因某道生产工序执行的偏差而产生。对于轧辊缺陷的研究和原因的排查， 是一项繁琐的工作，需要大量的检验和细致的分析。铸造工作者也常常受此困扰。 在实际生产中，我们发现离心轧辊加工后辊身表面出现大面积亮斑现象，亮斑形状不规则（见图 1）。宏观表 现为轧辊工作层表面有色差，亮斑处硬度与正常部位硬度相差5～10HSD 左右；微观表现为亮斑处碳化物聚集。 2 1 1 图 1 轧辊工作层表面亮斑 1—正常部位 2—亮斑部位 刘娜，女，硕士，铸造高级工程师， 从事离心轧辊制造技术研究和工艺设计， liunajc@ 关于离心轧辊辊身亮斑问题的探讨 8-371 1 轧辊检验 在生产中，我们选取了存在此类问题的离心合金球铁轧辊进行了硬度、金相组织检验和成分检测。 1.1 硬度检测