低品质大洋多金属锰结核还原熔炼试验的研究.pdfVIP

低品质大洋多金属锰结核还原熔炼试验研究 沈裕军 陈文如 （长沙矿冶研究院，长沙 410012 ） 摘 要 DY105-13 航次多金属结核含 Mn 低，Mn、Fe、Cu、Co、Ni 含量之和低，而含 P 高，是历次多金属结核 试样中质量较差者。本文研究了还原剂种类、配比及炉渣碱度对熔炼过程的影响，表明采用合适的还原剂制度与炉 渣碱度对 DY105-13 航次多金属结核矿进行还原熔炼，可实现锰与铜、镍、钴的高效分离,得到熔炼合金和质量合格 的富锰渣,为进一步回有价金属创造了条件。 关键词 大洋多金属锰结核 还原熔炼 富锰渣 熔炼合金 铜镍钴 Experimentation and Study on Reduction Smelting of Poor-Quality Ocean Polymetallic Nodules Shen Yujun Chen Wenru (Changsha Research Institute of Mining Metallurgy Co.,Ltd., Changsha，410012) Abstract DY105-13 cruise polymetallic nodules with low Mn, Cu, Co, Ni contents and high P content, is of poor-quality sample of polymetallic nodules. In this paper, reduction agent type, ratio and slag basicity on the impact of the reducing smelting process were investigated, indicating that efficient separation can be achieved between manganese and copper, nickel ,cobalt by using of appropriate reduction agent system and the slag basicity for DY105-13 cruise polymetallic nodules reduction smelting, getting molten alloys, acceptable quality manganese-rich slag and providing favourable conditions for further recovering them ． Key words ocean polymetallic nodules，reduction smelting ，manganese-rich slag ，molten alloys ，copper-nickel-cobalt 1 引言 大洋多金属锰结核广泛分布于世界各大洋底。含有 70 多种元素，主要含 Mn 、Fe 、Cu、Co、Ni ，还含 有 Mo 、V 、Zn 、W 、Ti、稀土及贵金属元素等，资源巨大，已成为世界瞩目的21 世纪具有商业开发前景的 战略矿产资源[1,2] 。美、德、法、日等西方发达国家和印、韩等发展中国家均投入大量人力和财力开展大洋 多金属锰结核资源的勘探及冶炼加工研究[3,4] 。 我国自“八五”开始，开展了十多个航次的大洋多金属锰结核矿的资源调查，同时为配合资源评价开展 了多金属锰结核矿的冶炼加工研究，重点开展了大洋多金属锰结核的还原熔炼-浸出及亚铜离子氨浸工艺的 研究。其中，还原熔炼-浸出工艺被认为是一种最具发展前景的并符合我国国情及国际海底多金属结核矿产 资源特点的冶炼工艺[5,6]，既考虑到 Cu、Co、Ni 的高效提取，同时根据我国冶金锰矿石短缺的国情，注重 Mn 的回收和利用。该工艺通过选择性还原熔炼，一步就能实现锰与有价金属铜、镍、钴的分离及富集，得 到富锰渣及富集了镍铜钴的熔炼合金，富