酸性环境用X65QS+无缝管线管焊接性能工艺试验.pdfVIP

酸性环境用 X65QS 无缝管线管焊接性能工艺试验 李 艳 郑 飞 赵春辉 赵游云 甄晓川 郝玉华 许文妍 （天津钢管集团股份有限公司技术中心，天津 300301 ） 摘 要 X65QS 抗腐蚀管线管具有良好的焊接性是其在石油和天然气工业应用的重要前提。在选定焊接方法、焊 接材料和工艺参数条件下, 进行了 X65QS 管线管试件焊接和接头性能试验。结果表明, X65QS 管线管具有良好的 可焊性, 焊接接头具有优异的抗腐蚀性能，选用的焊接材料和工艺参数可用于这种材料管道的现场焊接。 关键词 X65QS 无缝管线管 抗 H2S 腐蚀 焊接 Welding Experiment on X65QS Seamless Pipeline Steel for Sour Service Li Yan Zheng Fei Zhao Chunhui ZhaoYouyun Zhen Xiaochuan Hao Yuhua Xu Wenyan （Research and development center of Tianjin Pipe （Group ）corporation, Tianjin, 300301 ） Abstract It is important for the weldability of X65QS in oil and gas industry. The mechanical properties of welding and weldment have been conduct on X65QS pipeline steel under the selection of welding process, welding filler metal and parameter. The results show that the weldablity for use of X65QS pipeline steel is very good, the joint of X65QS after welding has a good ant-corrosion performance and the welding filler metal and parameter can be used for welding in field. Key words X65QS, SMLS pipeline steel, ant-H2S corrosion, welding 1 X65 钢级管线管是石油天然气工业系统急需的高钢级无缝输送管线，尤其是近些年输送环境的改变和加 强对输送安全的重视，抗 H [1] 2S 腐蚀高钢级管线管需求与日俱增 。无缝管在抗腐蚀和管道安全方面具有天然 的优势，是恶劣环境下输送管道首选管材。输送无缝管连接方式是通过管与管对接焊接方式连接的，可以通 过加长管线的长度减少焊接接头的数量，从而减少成本增加安全性，这需要管线材料具有很好的焊接性能和 止裂性能，因此开发出具有优异焊接性能和抗腐蚀性能的管线管是当前无缝钢管厂的首要任务。本文通过手 工电弧焊的焊接方式研究公司自行开发的 X65QS 抗 H2S 腐蚀管线管接接头处的焊接性能以及抗腐蚀性能。 1 X65QS 焊接 1.1 焊接试验材料 X65QS 无缝管线管为本公司 150t 电炉冶炼、LF 炉精炼、VD 高真空脱气处理，连铸成φ310 断面铸坯， 再经 MPM 连轧机组热轧工艺生产的规格为 237.1mm ×8.74mm 调质处理的抗腐蚀无缝管线管，具体化学成 分要求见表 1。同时要求B≤0.0005%，Ca≤0.006%，N ≤0.012%，Al/N ≥2 ，V+Nb+Ti ≤0.15%，Cr+Mo+Ni+Cu 李艳，女，硕士，工程师，从事抗腐蚀油井管及管线管的开发，liyantpco@163.com 酸性环境用X65QS 无缝管线管焊接性能工艺试验 ≤0.6% 。依据API SPEC 5L[2]公式计