CuO掺杂对高磁导率MnZn软磁铁氧体性能的影响.pdfVIP

CuO掺杂对高磁导率MnZn软磁铁氧体性能的影响 王宏，王京平，窦海之 (广东风华高新科技股份有限公司，广东肇庆526020) 摘要：采用传统的氧化物湿法工艺制备CuO掺杂的高磁导率MnZn软磁铁氧体。研究了CuO掺杂对材 料烧结特性、微观结构及电磁性能的影响。结果表明，适量的CuO掺杂在确保材料起始磁导率的条件下，有效 关键词：MnZn铁氧体；CuO掺杂；电磁性能 中图分类号：TM277+．1 文献标识码：B 文章编号：1001．3830(2009)04．0037．03 EffectsofCuO onthe of Initial DopantPropertiesHigh MnZnFerrite Permeability WANG Hai—zhi Hong，WANG Jing—ping，DOU Advanced GuangdongFenghua 526020,China Technology(Holding)Co，Ltd,Zhaoqing softMnZnferritewithCuO was traditionaloxidewet andthe Abstract：High∥i dopantpreparedusing process effectsofCuO wereresearchedonthe and dopant smteringcharacteristics，microstructureelectro-magneticproperties． Theresultsshowedthata amountofCuO can reducethe the proper dopanteriectively sinteringternperature．increase cut．0fr the characteristicsofthematerialwithout itSinitial frequency,enhanceimpeda【nee decreasing permeability． for 0．1wt％CuO Better wereobtained at generalproperties Mn048Zn047Fe2．0504withdopantfiring1325℃，fli=10860， coil Z=1420f1． ％=125℃，Z=250kHz，core impedance Soft words：MnZnferrite；CuO Key dopant；electromagneticproperty 软磁铁氧体材料的性能。因此，具备高频、高阻抗 1引言 和高磁导率特性的软磁铁氧体材料成为一个重要 随着高新技术的不断发展，数字技术在电子产 的研究课题。