Trans. Nonferrous Met. Soc. China 24(2014) 2991−3000 Kinetics analysis of non-isothermal decomposition of Ag2O−graphite mixture Seyed Hadi SHAHCHERAGHI1, Gholam Reza KHAYATI2 1. Department of Mineral Processing Engineering, Shahid Bahonar University of Kerman, Kerman, Iran; 2. Department of Materials Science and Engineering, Shahid Bahonar University of Kerman, Kerman, Iran Received 6 November 2013; accepted 27 February 2014 Abstract: The thermal decomposition kinetics of Ag O−graphite mixture was systematically studied using a differential scanning 2 calorimeter (DSC) in terms of model-fitting Malek approach, integral master plot method and model-free advanced isoconversional method of Vyazovkin. The results showed that the thermal decomposition occurred in two stages. The first step was the decomposition process of Ag2O to form porous silver particles as a complex process with the participation of at least two mechanisms, and the second step corresponded to the structural change from porous particles to silver bulk crystals as a single-step process. Key words: Ag2O; advanced isoconversional method; kinetic modeling; Sestak–Berggren model interface controlled, respectively. 1 Introduction To the best of our knowledge, there is not a great deal of information in literature about the kinetics of the Silver (I) oxide is a highly thermally stable silver thermal or thermochemical decomposition of Ag2O.