微波辐照稻杆制造活性炭.pdfVIP

林产化学与工业990317 林产化学与工业 CHEMISTRY AND INDUSTRY OF FOREST PRODUCTS 1999年　第19卷　第3期　Vol.19　No.3　1999 微波辐照稻杆制造活性炭 彭金辉　张世敏　张利波 摘　要：　研究了微波辐照经氯化锌浸渍的稻杆制造活性炭。实验结果表明，经微波辐照8 min，所 得活性炭的亚甲基蓝脱色力为15 mL/0.1 g，为国家标准一级品(LY 216-79)的1.25倍，时间仅为传统方 法的1/45。 关键词：　微波辐照；稻杆；活性炭 中图分类号：TQ 424.1　　　文献标识码：A　　　文章编号：0253-2417(1999)03-0088-03 MANUFACTURE OF ACTIVATED CARBON FROM RICE STEM BY MICROWAVE RADIATION PENG Jin-hui, ZHANG Shi-ming, ZHANG Li-bo (Department of Metallurgy,Kunming University of Science and Technology,Kunming 650093，China) Abstract:In this paper,the new process of manufacturing of activated carbon from rice stem leached with zinc chloride by microwave radiation is reported.According to the experimental data,the microwave processing is 45 times as fast as the conventional processing,and the methylene blue decolorizing ability is 1.25 times as strong as that of the first grade in standard of powder activated carbon of China(LY 216-79). Key words:microwave radiation;rice stem;activated carbon 　　随着社会经济的发展和人民生活水平的提高，使活性炭应用领域不断拓宽，需求量越来越大， 对活性炭质量的要求也越来越高。因此，改革传统活性炭生产工艺，进行活性炭新工艺的研究和开 发势在必行。本课题组曾分别进行了微波辐照经氯化锌或磷酸浸渍的废木屑、栲胶废料、蚕豆壳制 造活性炭的研究，均取得了较好的效果 ［1～8］ 。然而，微波辐照经氯化锌浸渍的稻杆制造活性炭的 研究尚未见报道。本文进行微波辐照稻杆制造活性炭的研究，旨在实现农业废弃物的再生并寻求活 性炭新工艺。 1　实验 1.1　原料 　　稻杆取自云南省某地。氯化锌为98 %工业级，盐酸＞31 %。 1.2　试验方法和装置 　　稻杆破碎至5 mm左右，与氯化锌溶液混合浸渍15 h后，装在石英坩埚中，放入多模微波腔体中 进行辐照，随后对辐照产品进行漂洗、烘干、粉碎和筛分，得到粉状活性炭产品。实验装置如图1所 示。实验装置中，微波频率为2.45 GHz,微波最大功率为800 W。 　　氯化锌溶液的浓度为50 %(wt)，稻杆(干)∶氯化锌=1∶3.5。 　　采用林业部LY 216-79标准测定产品指标。 万方数据 file:///E|/qk/lchxygy/lchx99/lchx9903/990317.htm（第 1／3 页）2010-3-23 3:17:27 林产化学与工业990317 图1　实验装置简图 Fig.1　Experimental equipment 2　实验结果与讨论 2.1　实验结果