2012 年钢锭制造技术与管理研讨会论文集    2012 年 5 月  惰性气体保护电渣冶炼铁路用 G20CrNi2MoA 渗碳轴承钢 丁磊 苏春阳 潘明旭 张洲 柳学胜 （湖北新冶钢有限公司，黄石 435001 ） 摘 要 介绍了惰性气体保护电渣炉的设备特点，在全封闭气罩内经氩气保护与非气体 保护冶炼的铁路用渗碳轴承钢 G20CrNi2MoA 的对比试验结果表明：使用氩气保护电渣炉冶 炼的电渣钢锭各部位合金元素烧损少且分布均匀，钢中气体及非金属夹杂物含量低，冶金质 量明显优于非气体保护电渣炉。 关键词 惰性气体保护电渣炉 渗碳轴承钢 氧含量 非金属夹杂物 Inert Gas Protection Electroslag Remelt Railway Carburizied  Bearing Steel G20CrNi2MoA  Ding lei, Su chunyang, Pan mingxu, Zhang zhou, Liu xuesheng ( Hubei Xinyegang Steel Co Ltd, Huangshi 435001) Abstract The features of inert gas protection electroslag furnace are introduced. The carburizied bearing steel was remelted under inert gas in closed hood and at atmosphere. From the comparision, the characteristics of less burning loss of alloying elements, well-distributed, less gases and nonmetallic inclusions in the electroslag ingot which remelted under inert gas are presented. And its metallurgical quality is much better than non-gas protection electroslag furnace’s. Material Index Inert Gas Protection Electroslag Furnace, Carburizied Bearing Steel, Oxygen Content, Nonmetallic Inclusions 传统的电渣重熔都是在大气环境下进行，60 年代的研究结果表明，重熔钢中的氧含量 取决于脱氧元素的浓度和该脱氧元素的氧化物在渣中的活度，此外，渣池上方大气环境下的 氧分压也会产生一定的影响。过去的工作者为了降低钢中氧含量，通常在重熔过程中向渣池 界面加入诸如 J-Al 、J-Mg 、Ca-Si、Fe-Si 等脱氧剂对熔渣进行连续脱氧，但这种方法将会改     127 2012 年钢锭制造技术与管理研讨会论文集    2012 年 5 月  变熔渣的成分，从而使重熔钢锭中的易氧化元素发生变化，甚至达不到标准或工艺要求。近 年来，国内外对惰性气体保护电渣炉及重熔工艺的研究进展较快，在防止电渣钢锭增氢的同 [1] [2] 时，也可以有效地防止钢锭增氧 ，而降低氧含量有利于提高轴承钢的疲劳寿命 。 本文简要地介绍了 5t 惰性气体保护电渣炉设