Nano-precision combined process of electrolytic in-process dressing grinding and magnetic assisted polishing on optics glass material.pdfVIP

Transactionsof NonferrousM etals SocietyofChina ELSEVIER Press Trans．NonferrousMet．Soc．China19(20091s301一s306 www ．tnmsc．cn Nano—precisioncombinedprocessofelectrolyticin--processdressinggrinding andmagneticassistedpolishingonopticsglassmaterial Tae-SooKWAK，Yong—ChulLEE，Gyung—Nyunl(IM ，Dae—BongCHOI， M ikioYAMANOI．HitoshiOHM0RJ DepartmentofMechanicalEngineering，JinjuNationalUniversity,Jinju，Korea Received2March2009；accepted30M ay2009 Abstract：This study is focused on the application of an effective fabrication method combining electrolytic in-process dressing(ELID)grindingandmagneticassistedpolishing(MAP)tonano—precisionmirrorsurfacegrinding ontheoptics glass—ceramicnamedZerodurethatiscommonlyusedinprecisionopticscomponents．Theresultsshow thevariationofsurface roughnessafterMAPprocessesutilizingFe+CeO2，Fe+CeO2+diamondpasteandFe+diamondpasteareappliedtoELID rgound surfaces．TheMAPsurfaceroughnessesforELIDrgoundsurfaceroughnesses a)of52．1，39．8and51．1nmusing#1200grinding wheelareimprovedto6．1，4．6and1．9nm，respectively．ThesurfaceroughnessofMAPprocessusingFe+CeO2+diamondpasteis superiortothatusingotherprocesses．MoreoveL ittakeslessthan 10mintoconducttheMAPprocesses．Thecombinedmethod suggestedeffectivelyreducestheworkingtimetogettherequiredsurfacequalities． Keywords：electrolyticin—-processdressing；magneticassistedpolishing；nano—precision；mirrorsurfacefinishing adoptedasafinalfinishingprocessafterELID grinding 1Introduction