45钢断面收缩率与白点的关系.doc

45钢断面收缩率与白点的关系 逯 登 尧 （山东寿光巨能特钢有限公司，山东 寿光262711） 摘　要：通过对45钢两种试样状态及冶炼、轧制工艺的分析，找出了白点是导致45钢断面收缩率不合的根本原因，钢中氢含量高是内因，轧后冷速过快是外因。从源头上减少钢中氢含量及轧后缓冷的措施，可解决由白点引起的塑性偏低问题。 关键词：45钢；断面收缩率；白点；氢脆；缓冷 中图分类号：TG113.25　　 文献标识码：A　　 文章编号：1004-4620（2008）03-0052-02 Relation of Between Area Reduction of 45 Steel and Flakes LU Deng-yao （Shandong Shouguang Juneng Special Steel Co., Ltd., Shouguang 262711, China） Abstract: By analyzing the states of two samples and smelting and rolling process, it was found out that the essential reason resulting in area reduction disqualification of Steel 45 was flake. The high hydrogen content in the steel was internal reason and the fast cooling speed after rolling was external factor. Reducing hydrogen carried from slagging material and process and adopting slow cooling after rolling can resolve the question of the low plasticity caused by flakes. Key words: 45 steel; area reduction； flake; hydrogen brittleness; retarded cooling 1 前 言 　　山东寿光巨能特钢有限公司Φ550×1/Φ430×4+Φ320×6小型轧钢生产线自2004年投产以来，主要生产45、20等碳素结构钢，生产规格为φ16～φ60 mm。在生产检验过程中，发现45钢部分炉号的塑性值偏低，主要是断面收缩率达不到标准要求。2005年3月初，45钢断面收缩率复验率达到28.5%，严重影响了该生产线的组织和协调。为此组织了对该问题的技术攻关，查找原因、采取措施，确保轧钢生产线稳定、顺行，使出厂钢材完全达标。 2 检测与分析 　　钢材产生断面收缩率不合的原因很多，如化学成分不合、钢中非金属夹杂物含量高、内部疏松严重、内裂等均会引起钢材的塑性降低。共检验2005年3月6日至4月10日生产的45钢228炉，规格为φ30～φ60 mm，因断面收缩率不合导致复验的共65炉，复验率达到28.5%，复验后全部合格（统计结果见表1）。为了查找原因，对这65炉断面收缩率不合的炉号进行了一系列统计分析。 表1? 钢材的力学性能统计结果 项目 σs/MPa σb/MPa ψ/% δ5/% 初验 355～420 388.1 610～685 646.0 19～42 30.5 16～25 20.2 复验 355～445 389.6 615～690 647.6 41～54 44.8 19～30 24.0 GB/T699 ≥355 ≥600 ≥40 ≥16 2.1 化学成分　　通过对化学成分的统计分析，未见有成分异常现象，全部符合标准要求（见表2）。 项目 C Si Mn P S Cr Ni Cu GB/T699 0.42～0.50 0.17～0.37 0.50～0.80 ≤0.035 ≤0.035 ≤0.25 ≤0.30 ≤0.25 实测 0.43～0.49 0.46 0.20～0.28 0.23 0.54～0.61 0.57 0.007～0.026 0.013 0.004～0.022 0.009 0.03～0.09 0.05 0.02～0.04 0.03 0.05～0.10 0.07 2.2 低倍组织　　通过对缓冷前钢材低倍组织检验结果的统计分析，除个别炉号存在内部裂纹外（见表3），其他无异常现象，全部符合标准要求（见表4）。 工艺 项目 总炉数 内裂炉数 内裂纹长度/mm 内裂炉数占总炉数比例/% 最长 最短 缓冷前 初验不合 65 8 3.5 1 12.3 初验合格 163 25 3.5 1 1