GD-APC杂化聚合材料在湿烟囱防腐改造中应用.docVIP

GD-APC杂化聚合材料在湿烟囱防腐改造中的应用 白学利 王玉山 郎鑫焱 和雄伟 （山西漳山发电有限责任公司，山西 长治 046021） 摘要：山西省某火电烟囱原采用粘贴泡沫玻璃砖防腐工艺，投产一年后，钢内筒多处腐蚀穿孔现象。为彻底解决烟囱严重腐蚀问题，从多项防腐改造方案中选用GD-APC杂化聚合材料防腐新工艺，这也是该材料首次在湿烟囱防腐改造工程中的应用。经过半年的施工，完成烟囱GD-APC防腐改造工程。在投运半年之际，电厂安排停炉检查烟囱防腐使用情况，发现GD-APC防腐性能良好。实施烟囱防腐改造过程中，电厂积累、总结了很多实用经验，也为湿烟囱腐蚀问题的解决探索了一条新工艺。 关键词：GD-APC杂化聚合材料 防腐 改造 施工 The application of GD-APC hybrid polymer materials in the wet stock corrosion transformation Bai Xue-li， Wang Yu-shan ， Lang Xin-yan，He Xiong-wei Shanxi Zhangshan Power Generation Co.,Ltd, Changzhi．Shanxi 046021,China Abstract：. A thermal power chimney use the pasting foam glass tile corrosion process at first in Shanxi Province, after one year since it was putted into operation there are many corrosion and perforated of the inner steel cylinder. To solve the severe corrosion problems in the chimney, Using the new anti-corrosion process of GD-APC Hybrid polymeric materials from a number of corrosi rehabilitation programs, This is also the first time that the material was used of corrosion Improvement Project in the wet chimneys.The renovation project of the GD-APC in chimney was completed after six months of construction.on the occasion of putting into operation in six months, the power plant shutdown and check the situation of the use of anti-corrosion in chimney ,found that the function of GD-APC anti-corrosione is good. During the process of implementing the Chimney corrosion transformation,power plants accumulated and summarized a lot of practical experience, and also explored a new technology.for the corrosion problems of wet stack. Key words： GD-APC hybrid compsite ， anti-corrosion ，transform ，construction 1 工程概况 山西省某火电厂2×600MW机组安装湿法脱硫装置(无GGH)，采用170米双管式自立烟囱，一台炉配一根直径6.5米的钢内管排烟，两台炉合用一座钢筋混凝土外筒，原采用TDN耐酸耐热粘剂、粘贴国产泡沫玻璃砖防腐工艺，烟囱分别于2008年3月投入使用。2009年2月，发生泡沫玻璃砖“飞出”烟囱现象，经停炉检查，泡沫玻璃砖脱落较多。经过2次修补，重新粘贴泡沫玻璃砖，但仍然有脱落现象，而且钢内筒多处出现腐蚀穿孔情况。 2 湿烟囱腐蚀原因简述 未安装GGH的脱硫装置排烟温度低、冷凝酸水量大，与之配套的烟囱简称“湿烟囱”。因湿法脱硫对烟气中的SO3脱除效率很低，不设GGH的脱硫排烟温度约在45℃－50℃，饱和湿度很大，冷凝结露液体