纯钛和镍铬合金口腔材料细菌粘附性能比较.docVIP

纯钛和镍铬合金口腔材料细菌粘附性能比较 　　【摘要】 目的 探究与分析纯钛和镍铬合金口腔材料细菌粘附性能。方法 选取纯钛和镍铬合金两种牙科常用修复材料， 分别制备成3.0 cm×2.0 cm×2.0 cm的板片试件， 每组5片。对两组的试件表面均给予抛光处理， 确保试件的表面无明显差异。实验菌株选用变形的链球菌， 将其悬浮放置于试件的表面上， 于37℃的环境中进行培养， 共培养48h， 后对粘附在材料表面的细菌再次进行洗脱、培养与菌落计数， 后对试验结果进行统计分析。结果 纯钛较镍铬合金相比表面粗糙度较高， 细菌总量较低， 差异具有统计学意义（P0.05）。结论 纯钛相比于镍铬合金具有更好的抗细菌粘附性， 值得推广与应用。 　　【关键词】 纯钛；镍铬合金；口腔材料；细菌粘附性能 　　【Abstract】 Objective To investigate and compare bacterial adhesion between pure titanium and nichrome as dental material. Methods Pure titanium and nichrome were made into 3.0 cm×2.0 cm×2.0 cm plates， and each group contained 5 plates. Polishing was made in both groups to ensure no obvious difference. Streptococcus mutans， as experimental strain， were placed on suspension over plate and taken in culture for 48 h under 37℃. Statistical analysis was made on experimental outcomes after elution， culture and colony count. Results Pure titanium showed higher surface roughness and lower total bacteria amount than nichrome， and their difference had statistical significance （P0.05）. Conclusion Pure titanium provides better bacterial adhesion than nichrome， and it is worth promoting and applying. 　　【Key words】 Pure titanium； Nichrome； Dental material； Bacterial adhesion 　　随着口腔医学技术的不断发展， 口腔材料也随之不断的进步， 而这些材料的抗菌性能及抑菌性能开始逐渐成为绝大多数临床医师关注的重点， 在研究中发现， 填充材料的菌斑粘附不仅可造成龋齿充填物脱落等情况， 同时可对修复质量、牙齿的美观度等造成影响[1]。现临床工作中为了减少细菌在材料表面发生沉积， 多配合使用抗菌剂， 以达到抑菌或杀菌的作用与目的。现本院针对较为常用的纯钛和镍铬合金两类口腔材料的细菌粘附性能展开研究， 结果总结报告如下。 　　1 材料与方法 　　1. 1 材料与仪器 选取纯钛和镍铬合金两种牙科常用修复材料（上海医疗器械股份有限公司齿科材料厂， 生产批号分别20150818）， 变形链球菌血清C型菌株（北京口腔医院研究所， 生产批号， 轻唾培养基的主要成分则包括：葡萄糖、蔗糖、胰蛋白胨、大豆蛋白胨等。 　　1. 2 试验方法 选取纯钛和镍铬合金两种牙科常用修复材料， 分别制备成3.0 cm×2.0 cm×2.0 cm的板片试件， 每组5片。对两组的试件表面均给予抛光处理， 抛光选择4000号的砂纸， 并采用精密粗糙度测试仪对表面的粗糙度进行测定， 每试件选取3个点， 结果取平均值， 确保试件的表面无明显差异。实验菌株选用变形的链球菌， 采用轻唾固定培养基对其进行激活、冻干、增菌， 转入至轻唾液体后， 培养其浓度为106 CFU/L的菌悬液， 所设定的培养条件为微厌氧（即80%的氮气、10%的氢气、10%的二氧化碳）， 将其悬浮放置于试件的表面上， 于37℃的环境中进行培养， 共培养48 h[2]。将试件取出后， 采用灭菌生理盐水对试件表面进行处理， 将没有粘附的菌落清除后， 放入至5 ml的灭菌生理盐水试管中， 震荡30 s以后采用倍比稀释法将其稀释至1/1000