养护剂DPS在水利工程中的应用研究.docVIP

养护剂DPS在水利工程中的应用研究 　　摘要：探讨了养护剂DPS对混凝土耐久性能的影响，并与普通混凝土进行了对比。结果表明：喷涂养护剂DPS以后，混凝土的抗渗性能、抗冻性能、抗氯离子渗透性能和抗碳化性能均有所提高，混凝土薄板微裂纹也大大减少。工程应用一年后，混凝土的抗渗性能和抗碳化性能仍强于未施用DPS的混凝土50%以上。 　　关键词：养护剂；渗透性；耐久性 　　中图分类号：TV43文献标志码：A文章编号： 　　1672-1683（2015）001-0120-02 　　Applied research of curing agent DPS in water conservancy project 　　ZHANG Lei 　　（PRCMWR of Science and Technology Promotion Center，Beijing 100038，China） 　　Abstract：Discusses the curing agents DPS on the properties of concrete durability，and then compared with the ordinary concrete.The results show that after coating the curing agent DPS，the permeability resistance，frost resistance，resistance to chloride ion permeability and carbonation resistance of concrete performance are improved，micro cracks concrete sheet also greatly reduced.The permeability resistance and carbonation resistance of concrete performance is still better than not more than 50% of the application of DPS concrete that after a year of engineering application. 　　Key words：curing agent；permeability；durability 　　南水北调工程是解决我国北方水资源严重短缺的特大型基础设施项目，对于我国经济的可持续发展具有重要的战略意义。南水北调工程东线和中线输水干线全长约2 900 km，其中采用混凝土衬砌的渠道要求混凝土防水、抗冻、防渗，保障混凝土结构的耐久性达到100年，除应从原材料、外加剂、施工工艺等方面控制混凝土质量，还需加强混凝土养护等关键环节。 　　传统的养护方法包括洒水法、湿砂覆盖法、塑料薄膜覆盖法、蒸汽养护法等。这些方法均存在不同程度的缺陷，浪费资源，且养护质量欠稳定，复杂部位难以养护，这与工程建筑现代化的发展已经不相适应。国内外专家从20世纪40年代开始研究化学养护剂，研发了各种产品，并在实际工程中得以应用，取得了良好的社会效益和经济效益[1-5]。 　　本研究采用的养护剂为永凝液DPS（Deep Penetration Sealer），其在实际工程中常作为渗透结晶型防水材料使用，作用效果良好[6-7]。由于永凝液DPS为液状材料，将其喷洒在混凝土表面后，渗入混凝土内部，与混凝土中的游离碱产生化学反应，生成稳定的枝蔓状晶体胶质，有效地堵塞混凝土内部微细裂缝和毛细空隙，使混凝土表面与空气隔绝，大幅度降低水分从混凝土表面蒸发损失，从而利用混凝土中自身的水分最大限度地完成水化作用，达到养护的目的，可用作养护剂。 　　1试验部分 　　1.1原材料 　　水泥：普通硅酸盐水泥（P?O42.5R）。 　　砂：中粗砂，细度模数为2.74。 　　石子：粒径为10～20 mm。 　　外加剂：高效引气减水剂（型号SKY-1）。 　　永凝液DPS：金字塔牌永凝液，在混凝土处理面喷涂用量为3 kg/m2。 　　1.2混凝土配合比 　　混凝土配合比见表1。 　　表1混凝土配合比 　　kg/m3 　　材料名称水泥砂石子外加剂水 　　用量3307541 1314.3165 　　1.3试验方法及依据 　　混凝土抗渗性、抗冻性、抗碳化性、Cl-扩散系数（电量法）等试验方法依据《水工混凝土试验规程》（SL 352-2006），抗渗试验试验完成后，试件表面均未出现渗水现象，劈开混凝土试件，测量渗透深度，得出渗透深度结果；有效保水率试验方法参照JC 901-2002《水泥混凝土养护剂》附录A；表面吸水率试验方