某铁矿石可选性研究.docVIP

某铁矿石可选性研究 　　摘要 安徽省某铁矿石进行了工艺矿物学分析后结果表明，该铁矿石中的铁主要以磁铁矿的形式存在，占总铁的92.32%。但是经过磁选后铁精矿含硫较高，针对该矿样进行了磁选后铁精矿反浮选脱硫实验，阶磨阶选―先磁后浮工艺探索实验，阶磨阶选―先浮后磁工艺探索实验。综合三种流程实验结果得出采用先浮后磁工艺可得到铁精矿品位67.32%，含硫0.134%，铁回收率71.85%的铁精矿。 　　关键词 磁选；浮选；反浮选；脱硫 　　中图分类号TD9 文献标识码A 文章编号 1674-6708（2014）110-0102-02 　　Study on Iron Ore Optional 　　Ma NiyaYang Huibing 　　 Anhui province Longqiao Mining Co.Ltd，Lujiang 231500， China. 　　 　　AbstractAn iron of Anhui province the mineralogical analysis results show that ，the iron ore in the iron mainly exists in the form of magnetite， accounted for 92.32% of iron. After mangnetic separation of iron concentrate with high sulfur content in the samples. Then the magnetic iron concentrate by reverse flotation desulfurization experiment、the stage grinding and stage selection first magnetic floating processexperiment、the stage grinding and stage selection flotation and magnetic technology experiments. Three comprehensive process experimental results obtained by flotation and magnetic technology can get iron concentrate grade of 67.32%， sulfur 0.134%， the recovery of iron 71.85% iron concentrate. 　　KeywordsMagnetic separation，Flotation，Reverse flotation，Desulphurization 　　 　　1矿石性质 　　安徽某铁矿石中磁性铁含量较高，占总铁的92.32%。脉石成分主要为SiO2。原矿化学多元素分析见表1。 　　成分 TFe mFe SiO2 CaO MgO TS mS P lg 　　含量 38.26 35.32 22.35 4.72 2.81 1.82 1.40 0.19 3.31 　　 　　表1原矿化学多元素分析结果% 　　2不同分选工艺试验 　　2.1磁选后精矿反浮选 　　采取磨矿10min后进行两段磁选，（磨矿后--0.076mm含量87%）磁选精矿再进行反浮选，实验流程图见图1。 　　磁选后实验结果见表2。 　　产品 产率 品位 回收率 　　 TFe S TFe S 　　铁精矿 49.94 62.18 2.58 80.01 68.9 　　一次磁选尾矿 48.15 14.42 1.07 18.11 27.55 　　二次磁选尾矿 1.91 17.56 3.44 0.88 3.55 　　原矿 100 38.33 1.87 100 100 　　 　　表2磁选实验结果% 　　 　　图1 磁选后反浮选流程 　　由表2可以看出，磁选后铁精矿中硫含量2.58%，明显超出了铁精矿对硫的质量要求，而硫主要是以磁黄铁矿的形式存在于原矿中，探索利用反浮选降低铁精矿中的硫品位，反浮选实验结果见表3 　　产品 产率 品位 回收率 　　 TFe S TFe S 　　铁精矿 97.16 62.33 2.30 97.35 86.95 　　硫精矿 2.84 58.01 11.91 2.65 13.05 　　原矿 100 62.21 2.57 100 100 　　 　　表3 反浮选实验结果% 　　由实验结果表明：采用单一的硫酸铜对磁黄铁矿进行活化效果并不明显，所以后续试验对浮选药剂制度进行了重新调整。 　　2.2 阶磨阶选――先磁后浮工艺