聚酯格栅冻融循环试验研究.doc

冻融环栅 程卫国1 刘丽佳2,3 孙景路 2,3 张 滨,3 （黑龙江 哈尔滨 150080. 黑龙江省水利科学研究院，黑龙江 哈尔滨 150080） Freezing-Thawing Cycle Effect on the Tensile Properties of Polyester Geogrids C, Sun Jinglu,3, Zhang Bin,3 (1.Jiangsu UniSure Block Co.,Ltd,,Jiangsu Nanjing ,China ,210005 2. Heilongjiang Seasonal Frozen Soil Region Engineering Frozen Soil Key Laboratory, Harbin, China, 150080 3. Heilongjiang Provincial Hydraulic Research Institute, Harbin, China, 150080) Abstract: Tensile properties of polyester geogrids were tested in laboratory at the temperature of 20℃。The geogrids were experienced 50 freezing-thawing cycles. Through the experimental research on the tensile properties of polyester geogrids ,the ultimate bearing capacity, maximum extensibility stress and elastic modulus for different extensibility of geogrids. The test results show that freeze-thaw cycles have little effect on the ultimate extensibility. With the increasing of freezing-thawing cycle, the ultimate extensibility of polyester geogrids and elastic modulus show linear decline.  Key words: polyester geogrids, freezing-thawing cycle, bearing capacity , extensibility ,elastic modulus 摘要：在20℃常温环境下，对经过50冻融循环后的S5050聚酯双向土工格栅进行拉伸试验。研究这些格栅的极限承载力、最大延伸率以及不同延伸率对应的应力值、弹性模量等数据。从试验结果看出冻融循环对材料的极限延伸率影响不大，基本没有变化，冻融循环使材料的极限承载力降低，并随着冻融循环次数的增长，极限承载力和弹性模量均呈线性下降。 关键词：聚酯格栅、冻融循环、屈服强度、延伸率、弹性模量 0、引言 S5050聚酯双向土工格栅的性质均匀稳定、抗拉变形模量大、强度高、韧性好、与土颗粒间的摩擦系数高、连锁作用强,因此在实际工程有着广泛的应用与发展前景。实验室中通常采用直接拉伸试验或在土中的拉拨摩擦试验来研究土工网格栅与土相互作用的界面反应机理,确定网土间的界面特性参数。在北方地区，由于土工格栅加筋挡土墙要经历长期的反复的冻融循环，还要充分考虑冻融循环对土工格栅力学性能的影响。为试验开冻融环条聚酯纤维栅测试冻融环对强响为试验装1.1、试验装SL/T 235-1999）拉伸试验相关规定。 试样冻融循环采用日本东芝公司的冻融循环机，工作温度范围-35℃～+60℃，控制精度：±0.1℃；拉伸试验采用LJ-1000型拉力试验机；数据采集采用DT515数字采集仪；拉力测试采用BLR-1型应力传感器；变形测试采用YHD-100型静态位移传感器。 1.2、试验试验规为S5050聚酯纤维栅产检测数见1。 产品名称 规格型号 材质 强度 （kN/m） 断裂伸长率 (%) 网格尺寸 (mm) 聚酯格栅 S5050 涤纶纤维 ≥45 ≤14 25.4×25.4 表1、聚酯格栅参数性能表 1.3、试样备1. 将S5050聚酯双向格栅SL/T 235-1999）拉伸试验规定制作试样并编号。 试样长300mm 试样宽3条条数20个。 2. 将制作好的试样进行冻融循环处理。冻融循环环境温 -20℃～+20℃，采取空气中冻结6h，其中冻结历时4h，融化历时2h，试验对S5050聚酯