包钢现阶段生产工艺流程中铌的走向分析.pdfVIP

包钢现阶段生产工艺流程中铌的走向分析 姜银举 1 蔺 瑞 1 方永辉 2 徐掌印 1 李保卫 1 （1. 内蒙古科技大学材料与冶金学院，包头，014010；2. 包钢（集团）公司，包头，014010） 摘 要 本文采用电感耦合等离子体质谱 （ICP-MS ）法对包钢现阶段生产流程中的铁精矿、铁、高炉渣、钢、转 炉渣中铌的含量进行了分析，在分析数据的基础上计算得到了高炉过程铌的还原率和转炉过程铌的氧化率。对铌在 高炉和转炉冶炼过程中的冶金原理进行了探讨。 关键词 铌冶金 还原和氧化 包钢 Analysis on the Change of Niobium Content in the Current Metallurgical Process of Baogang Jiang Yinju 1 Lin Rui 1 Fang Yonghui 2 Xu Zhangyin 1 Li Baowei 1 (1. Inner Mongolia University of Science and Technology, Baotou, 014010; 2. Baotou Iron Steel Corp., Ltd., Baotou,014010) Abstract The concentration of niobium in iron, blast furnace slag, steel and converter slag in the metallurgical process which is currently used at Baogang was studied using inductively coupled plasma-mass spectrometry (ICP-MS ). Based on the experimental result, reduction efficiency of niobium in the blast furnace process and oxidation efficiency of niobium in the converter process was calculated and the niobium metallurgy in the both processes was discussed. Key words niobium metallurgy,reduction and oxidation,Baogang 白云鄂博矿 Nb O 含量为 0.08%～0.14%，由于铌的难选性，部分铌进入包钢生产工艺流程，铁精矿、 2 5 铁水、钢中均含有微量的铌。文献报道包钢以白云鄂博铁精矿为原料生产的（20 世纪60～80 年代） 产品的铌含量：在铁水中含铌 0.1%左右[1]，在钢中含铌 3～5 ppm[2]，但生产工艺流程中详细的铌的 走向及其氧化还原情况，未见相关报道；另外，包钢现阶段的生产原料及工艺发生了一些变化，为此，进行 了本文的工作，以期为后续的研究工作提供基础数据。 1 取样及分析方法 1.1 取样方法 本文只考虑选矿工艺后的冶金部分， 因此样品分析从炼铁厂精矿仓开始。 包钢的生产工艺流程如图1 所示。 由包钢炼铁厂精矿仓中取铁精矿样品。目前包钢炼铁厂高炉为了降低白云鄂博矿中K 、Na 、F 等有害元 素对高炉冶炼的不利影响，炼铁原料中，除白云鄂博矿铁精矿外，还配加了一定比例的外来矿铁精矿 （注： 这些外来矿中不含铌），由于外来矿的加入稀释了白云鄂博矿铁精矿中铌的浓度，所以从精矿仓中取样可以 确定进入高炉前铌的浓度。 跟踪取样铁精矿的走向，估计铁水从出铁口流出时间，在高炉出铁口取铁样和渣样；跟踪铁水走向，待 基金项目：包头市重大科技攻关项目“包头白云鄂博矿铌资源利用关键技术开发”，项目编号：2006Z1004 。 姜银举，教授，内蒙古包头市（014010 ）内蒙古科技大学材料与冶金学院，E-mail:jiangyinju3@126.com 2007 中国