毕业设计（论文） 题 目 阳极氧化制备二氧化钛纳米管机理及热处理对其影响 学 院 化学与化学工程学院 专业班级 学生姓名 指导教师 成 绩 2012 年6 月 20 日  摘 要 采用阳极氧化法，在NH4F+H2O的乙二醇溶液体系下制备了TiO2纳米管列阵薄膜，建立了TiO2纳米管列阵薄膜的“电场诱导”生长模型。TiO2纳米管的管形结构形成与TiO2的半导体性质相关。纳米管表面吸附的纳米粒子与管壁空间有关系。经过退火处理的纳米管管口有12~14个直径为25~35nm的纳米颗粒团聚体组成，600℃时，纳米管结构已被破坏。经过300~600℃之间不同温度处理后的TiO2纳米管呈现锐钛矿晶态，比表面积随温度升高呈下降趋势。 关键字：TiO2纳米管；阳极氧化；生长机理；热处理  Abstract In NH4F+H2O ethylene glycol solution,the TiO2 nanotube arrays were fabricated on the Ti substraet via anodic oxidation method at room temperatue.The induced electric-field growth model of TiO2 nanotube arrays was created. The formation of TiO2 nanotubes’tubular morphology is bound up with TiO2 semiconductor properties,The results show that there is relationship between nanoparticles on nanotube surface and space between walls. After annealing treatment,nanotube wall was comprised of 12~14 nanoparticles which the diameter of 25~35nm,and the nanotubes structure has been destroyed at 300~600℃.Specific surface area of nanotubes drop with temperature rise. Key words: TiO2 nanotubes；anodic oxidation；growth mechanism；annealing  目 录 摘 要 I Abstract II 第1章 绪论 1 1.1 TiO2 的晶体结构 1 1.2 二氧化钛纳米材料的存在形式 1 1.3 二氧化钛纳米管的制备方法 2 1.3.1 水热合成法 2 1.3.2 模板合成法 3 1.3.3 阳极氧化法 4 1.4 制备机理 4 1.4.1 水热合成法机理 4 1.4.2 模板法机理 5 1.4.3 阳极氧化法制备二氧化钛纳米管机理 5 1.5二氧化钛纳米管应用 7 1.5.1 光催化降解污染物 7 1.5.2 气敏传感器 7 1.5.3 其他方面的应用 7 1.6 本文的研究目的和内容 7 第2章 实验部分 8 2.1 实验用品 8 2.2 实验过程 8 2.2.1 钛片的预处理 8 2.2.2 电解液的制备 9 2.2.3 阳极氧化过程 9 2.2.4 样品的后处理 9 2.2.5 表征 9 第3章 结果与讨论 10 3.1 分析与讨论 10 3.1.1 SEM图片解析 10 3.1.2 阳极氧化制备TiO2纳米管机理 10 3.1.3 不同温度处理对TiO2纳米管的微观形貌的影响 14