Concrete temperature of reasons and countermeasures of cracks.docVIP

 PAGE \* MERGEFORMAT 10 Concrete temperature of reasons and countermeasures of cracks Abstract: The appearance of cracks will affect the structural integrity and durability even affect the structural safety of the structure thus affecting the life, how to eliminate the cracks into the design and construction should pay close attention to the link. Based on the crack Causes and treatment measures put forward their views. Keywords: concrete, temperature stress, crack, control A Preface In the modern construction of concrete plays an important role. And today, even though we take all measures to prevent the construction of the cracks, but the cracks still appear from time to time. The appearance of cracks will affect the structural integrity and durability, even will affect the safety of the structure thus affecting the structure of life. This article cracks in concrete construction far as the causes and treatment measures do a study. Cracks II Thermal expansion and contraction of concrete and wet up with thousands of shrinkage characteristics. Cracks for many reasons, mainly: temperature and humidity changes. The brittleness of concrete and uneven, as well as unreasonable structure, raw materials failed, Moban deformation and differential settlement of foundation. Fractures generally forms: plastic shrinkage cracks, settlement shrinkage cracks, condensation cracks, shrinkage cracks, temperature crack, crack carbon, the chemical reaction cracks, settlement cracks and frost cracks. concrete shrinkage deformation is mainly reflected, would cause shrinkage of concrete have great flexibility in its internal tensile stress, when the tensile stress of concrete anti-big tensile strength, the concrete surface will crack. The concrete to harden during the evolution of considerable heat of hydration of cement, the internal temperature rising, causing the surface tensile stress. Late in the cooling process, due to the constraints of basic o