年产量800万吨高炉—转炉长流程构造及分析.pdfVIP

年产量800 万吨高炉－转炉长流程构造及分析 贾国珍 姚彤辉 （东北大学国家环境保护生态工业重点实验室 沈阳 110004 ） 摘 要： 钢铁生产流程可分为高炉－转炉长流程和电炉短流程两大类，本文主要讨论长流程，构造了一个年产量 800 万 t 的薄板坯连铸连轧生产流程，确定了各工序对应的主体设备，分别分析和计算了各工序的工序能耗，通过对典型流程的分 析和研究，为我国同类钢铁企业的结构调整、流程优化提供参考，对钢铁企业提高资源、能源效率具有指导作用。 关键词： 长流程；工序能耗；吨钢能耗 Construct and Analyze an Long Flow that the Output is 8 Million Per year JIA Guo-zhen1 YAO Tong-hui2 （SEPA Key Laboratory on Eco-industry, Northeastern University, Shenyang, 110004） Abstract: Iron and steel production process can be divided into BF-BOF and EAF process long process short two categories, the paper mainly discuss long process. Construction of an annual output of 8 million t thin slab continuous casting and rolling production process. identified the processes corresponding to the main equipment. respectively analysis and calculation of the processes of energy consumption, Based on the typical flow analysis and research, similar to Chinas iron and steel enterprises, the restructuring process optimization for reference, in the iron and steel enterprises to improve the resources, energy efficiency is a guide. Key words: long flow, process energy consumption, Energy consumption for every tone of steel 年产量800万t/a 的薄板生产流程如下图所示： 1 构造不同类型钢厂制造流程的基本思想 2 3 烧结机（2×450m ）→高炉（2×4063m ）→转 和原则 炉(3×300t)→板坯连铸机（3 台2流）→热轧机（2 1）生产过程中金属物质流衰减“最小化” ，即 台宽2050mm ，窄1580mm） 收得率高、制造成本低； 主要技术指标如下： 2 ）生产过程中金属物质流温度起伏“最小化” 、 炉料采用烧结矿和球团矿，比例为烧结矿85 即节能、排放少、产品成本低等； ％，球团矿15 ％。其中，烧结矿、球团矿含铁量 3 ）生产过程时间以及中间过程库存量“最小 分别为59 ％和65 ％。焦比300kg/t ，喷吹煤粉 化” ，即劳动生产率高、成本低、交货期短等； 200kg/t ，铁钢比