Effect of alkaline solutions on the tensile properties of glass-polyester pipes.docVIP

APTEFF, 42, 1-288 (2011) DOI: 10.2298/APT1142185P UDC: 666.1.036.5+677.494.674]:54-145.16 BIBLID: 1450-7188 (2011) 42, 185-195 Original scientific paper EFFECT OF ALKALINE SOLUTIONS ON THE TENSILE PROPERTIES OF GLASS-POLYESTER PIPES Slavi?a S. Puti?*, Marina R. Stamenovi?, Jelena M. Petrovi?, Marko P. Rakin and Bojan I. Me?o? Univeristy of Belgrade, Faculty of Technology and Metallurgy, Karnegijeva 4, 11000 Belgrade, Serbia Construction materials, traditionally used in process equipment, are today success- fully replaced by composite materials. Hence, many pipes are made of these materials. The subject of this study was the influence of liquids on the state of stresses and tensile strengths in the longitudinal and circumferential direction of glass-polyester pipes of a definite structure and known fabrication process. These analyses are of great importance for the use of glass-polyester pipes in the chemical industry. The tensile properties (the ultimate tensile strength and the modulus of elasticity) were tested and determined for specimens cut out of the pipes; flat specimens for the tensile properties in the longitudinal direction and ring specimens for the tensile pro- perties in the circumferential direction. First, the tension test was performed on virgin samples (without the influence of any liquid), to obtain knowledge about the original tensile properties of the material composite studied. Subsequently, the specimens were soaked in alkaline solutions: sodium hydroxide (strong alkali) and ammonium hydroxide (weak alkali). These solutions were selected because of their considerable difference in pH values. The specimens and rings were left for 3, 10, 30 and 60 days in each liquid at room temperature. Then, the samples were tested on tension by the standard testing procedure. A comparison of the obtained results was made based on the pH values of the aggressive media in which