甘肃某微细粒嵌布磁铁矿选矿试验研究曹卫国(江西理工大学应用科学.doc

甘肃某微细粒嵌布磁铁矿选矿试验研究 曹卫国 (江西理工大学应用科学学院， 江西 赣州市341000) 摘要：甘肃某铁矿虽然以磁铁矿为主，但由于磁铁矿嵌布粒度微细，磁铁矿单体解离度很低。单一磁选流程磨矿粒度400目含量达85%，精选后精矿品位57%左右，精矿品位不达标。在原矿经过粗碎干选后，入选品位达到32.28%，经过磁选一重选联合流程，磨矿粒度300目含量达85%，最高可获得铁精矿品位66.16%，产率32.45%，回收率71.69%的较好指标。 关键词：微细粒嵌布磁铁矿；矿物组成；磁选；重选 中图分类号：TD922 文献标识码：A文章编号：1005-2763(2011)02-0035-03Experimental Study on the Beneficiafion of a Micro-fine Magnetite Ore from Gansu Cao Weiguo (School of Applied Sciences，Jiangxi University of Science and Technology，Ganzhou，Jiangxi 341000，China) Abstract：Although the main mineral in the iron ore from Gansu is magnetite，but because of micro-fine particle size distribution of magnetite，its monomer dissociation degree is low.Single magnetic separation process can obtain an iron concentrate grading 57% at a final grinding size of 85%一400 mesh，the Fe grade of Fe concentrate is substandard.After primary crushing and dry separation of the crude ore，an iron concentrate with Fe grade of 66.16%.Fe yield of 32.45% and Fe recovery of 71.69% can obtained by a combined process of magnetic separation and gravity concentration at a feed grade of 32.28%. Key Words：Micro-fine magnetite ore，Mineral composition，Magnetic separation，Gravity concentration 1试验矿样及矿样的相关性质1.1 矿样的制备 由于原矿品位(23%左右)较低，属贫磁铁矿，0～50mm左右，缩分后一600×630mm的磁滑轮，在磁场强度2100GS条件下选别后，经过中碎和细碎作为试验32.28%，抛去的尾矿品位11.34%，1。 1矿样制备流程 1.2矿石物质组成1。1 原矿化学成分分析结果 单位：% 矿石中金属矿物以磁铁矿为主，有少量的赤铁2。1.3 磁铁矿嵌布特征及其嵌布粒度 (1)磁铁矿呈浸染状、星点状、条带状分布于脉 表2 矿物相对含量 (2)钛铁矿呈板状、片状，沿黑云母、角闪石 (3)磁铁矿、黄铁矿呈不规则状，零星分布。 (4)褐铁矿呈片状微晶交代磁铁矿，沿磁铁矿 磁铁矿嵌布粒度微细，属微细粒嵌布类型，将有70%在+0.02mm以上粒级，30.25%在一0.02mm+0.04mm粒仅46.15%。 磁铁矿单体解离度很低，+0.076mm全部粒级0.076mm才有80.63%的0.045mm也只有91.33%的单体 2 试验方案的选择及试验 此矿石矿物组成较简单，金属矿物以磁铁矿为(见图2)。 2 阶段磨一阶段磁选探索流程 2.1磨矿粒度试验 实验采用400mm锥形球磨机，磨矿试验结果3。 3 磨矿试验结果 将矿样分别磨至200目含量占50%、80%和90%3个粒度进行弱磁选试验。2.2 弱磁选试验 矿样分别磨至200目含量占50%、80%和90%3个粒度进行磁选，弱磁粗选试验的磁场强度167kA/m，即2100GS。试验结果见表3。 从实验结果可知，在相同场强条件下，此铁矿石200目含量在50%和80%时，精矿品位37%左右，尾矿品位在11%左右，变化不大，而200目含量在90%时，精矿品位43.66%，尾矿品位10