开环聚合酚醛树脂制备覆膜砂的研究.pdfVIP

维普资讯 学兔兔 Apr．2008 · 388· VoI．57 NO．4 开环聚合酚醛树脂制备覆膜砂的研究 冀运东，王继辉，白会超 (武汉理工大学材料学院复合材料系，湖北武汉430070) 摘要：合成的双酚A型和苯酚型苯并恶嗪树脂，分别用其代替酚醛树脂制备了覆膜砂，并测试两种覆膜砂的性能。结 果表明：与酚醛树脂覆膜砂相比，新型覆膜砂的覆膜温度低，强度高，气味小，固化速度稍慢，是一种很有发展前景 的新型覆膜砂。 关键词：苯并恶嗪；开环聚合；覆膜砂 中图分类号：TG221 文献标识码：A 文章编号：1001—4977(2008)04—0388—03 Preparation of Coated Sand Using Ring--Opening Polymerization Phenolic Resin JI Yun—dong．WANG Ji—hui．BAI Hui—chao (School of Materials，Wuhan University of Science and Technology，Wuhan 430070，Hubei，China) Abstract：The bisphenoI-A type and phenol type benzoxazines are synthesized，which iS used to prepare coated sand instead of phenolic resin．The properties of the new resin coated sand and conventionaI phenolic resin coated sand are tested and compared．The results show that the benzoxazines resin coated sand has advantages as lower coated temperature，higher strength and smaller odour．It is a new type of coated sand with good development prospe~，although its curing time is a little longer． Key words：benzoxazines；ring—opening polymerization；resin coated sand 普通酚醛树脂覆膜砂中的树脂是热塑性酚醛树脂， 中，冷水浴并搅拌，反应l h。加入称量好的双酚A，同 固化剂是乌洛托品，这是一种酚醛缩聚体系。这种体系 时开始缓慢加热，0．5 h后温度升高至指定的温度。此 的优点是固化速度快，线性酚醛树脂的软化范围较宽， 时，保温回流l h。最后减压脱水，真空度在一0．085 MPa 固化反应中有水分子放出，而且气味比较大，树脂覆膜 以下，反应液不再有气泡产生，停止反应，倒出。得到 温度比较高，强度比较低。与缩聚反应不同，开环聚合 双酚A型苯并恶嗪树脂记为Ra。用苯酚代替双酚A，其 的最大特点是固化过程没有小分子放出，是一种先进的 他同上，相应获得苯酚型苯并恶嗪树脂记为Rb。 酚醛聚合形式。理论上，凡是酚醛树脂的应用领域和市 测试树脂项目如下，红外光谱：采