荒漠地区改性沥青流变性能试验分析 　　摘要：为了研究荒漠地区两种常用沥青流变性能，采用DSR、BBR的试验方法分别对RTFOT短期老化前后沥青的流变参数进行对比分析，得出短期老化前后沥青性能排序。结果表明：高温下RTFOT前后沥青流变性能顺序为橡胶改性沥青SBS改性沥青；低温下沥青RTFOT前流变性能顺序为SBS改性沥青橡胶改性沥青，而沥青RTFOT后低温流变性能顺序为橡胶改性沥青SBS改性沥青。研究表明在荒漠地区橡胶改性沥青的流变性能优于SBS改性沥青，短期老化提升了沥青抵抗流动变形的能力 Abstract： In order to study the theological properties of two kinds of asphalt used in desert area， the DSR and BBR test methods are used to compare and analyze the rheological parameters of asphalt before and after the short-term aging of RTFOT and obtain the asphalt performance sort before and after the short-term aging. Results show that， under high temperature， the asphalt rheological properties order before and after RTFOT is rubber modified asphalt SBS modified asphalt， under low temperature， the asphalt rheological properties order before and after RTFOT is SBS modified asphalt rubber modified asphalt， the rheological property order of asphalt at low temperature after RTFOT is rubber modified asphalt SBS modified asphalt. Research shows that rheological property of rubber modified asphalt is better than that of SBS modified asphalt in desert region， and short-term aging improves the ability of asphalt to resist flow deformation. 关键词：短期老化；流变性能；DSR；BBR Key words： short-term aging；rheological property；DSR；BBR 中图分类号：U416.217 文献标识码：A 文章编号：1006-4311（2016）19-0152-03 0 引言 荒漠地区现有道路以沥青路面为主，随着丝绸之路经济带的建设，重载交通现象严重，路面破坏非常普遍。加之荒漠地区夏季炎热、冬季寒冷，冷热悬殊，降水极少，蒸发旺盛等特殊气候使得沥青路面病害明显有不断加重的趋势。SHRP研究结果表明，沥青性能对高温流变性的影响为40%，对低温流变性的影响更到达了80%。然而，现有的研究却对荒漠地区改性沥青进行抗老化性能的分析却很少之又少 基于此，本文选取荒漠地区两种常用改性沥青运用动态剪切流变仪（DSR）、弯曲梁流变仪（BBR）测定旋转薄膜烘箱（RTFOT）试验前后沥青的流变参数，并进行系统分析。研究结果可为荒漠地区大温差条件下长寿面沥青路面提供理论支撑和技术指导 1 试验 1.1 试验原理 DSR是测定沥青高温流变性质的仪器。G*/sinδ是PG规范中衡量沥青高温抗车辙性能的参数。由于G*/sinδ能综合表征出较大的G*和较小的δ，因此在最高路面设计温度下，G*/sinδ值越大越好。规范要求：①原样沥青：G*/sinδ≥1.0kPa；②RTFOT后残留沥青：G*/sinδ≤2.2kPa BBR是测定沥青低温流变性质的仪器。SHRP规范要求：①劲度模量：S≤300MPa，S愈小，其低温柔性愈大，抵抗荷载的能力愈强；②劲度曲线斜率：m≥0.3，m值愈大，松弛性能愈好，沥青路面发生低温开裂的机会愈低 RTFOT主要是模拟沥青在加热拌和、铺筑过程中发生的变化，正是这个过程发生了沥青最重要的热老化反应 1.2 试验方案