厚板焊缝TOFD检测及其与传统检测方法的比较.pdfVIP

厚板焊缝TOFD检测及其与传统 检测方法的比较 李衍 (江苏太湖锅炉股份有限公司，无锡214187) 摘要：对板厚100mm的承压设备钢焊缝，采用ASME规范认可的超声衍射时差(TOFD) 法检测，灵敏度和缺陷检出率明显优于直线加速器和手工超声检测。将新技术与传统的缺陷评价 方法作了比较分析，并通过实例，指出新技术对检测结果的验收特点。 关键词：超声检测；TOFD法；射线照相；验收标准；缺陷评价 中图分类号：TGll5．28文献标识码：A 文章编号：1000-6656(2007)12—0722—04 NondestructiveEvaluationof ThicknessWelds： High BetweenTOFD andTraditionalMethods Comparison Technique LlYan TaihuBoiler (Jiangsu Co．Ltd．。Wuxi214187，China) of thicknesswelds than100mmin advanced Abstract：For pressureequipment-using inspectionhigh greater ultrasonic ASME achievedflaw and TOFD(time-of-flightdiffraction)techniqueacceptedby Code，the sensitivity ofdetectionare betterthantheone linearacceleratorandmanualultrasonicmethods． probability substantially by offlawevaluationbetweenthenew andthetraditionalmethodswasdrawn．The Comparison technique in results illustratedwithsome characteristicsofthenew ofthe were techniqueacceptanceinspection practical examples． offlaws Keywords：Ultrasonicexamination；TOFDtechnique；Radiography；Acceptancecriteria；Evaluation 术，信号较明显。美ASME锅炉压力容器规范自 1厚板焊缝检测现状 对板厚1001TUTI的承压设备焊缝，通常先用case)2235，近几年欧、日也都有应用。 超声波作100％手工检测，再用4MeV以上直线加 速器作适当比例的射线照相。手工超声要在焊缝两 规定了超声检测取代射线照相的最低要求，也规定 面四侧，用2～3种折射角对焊缝横断面作分层扫 了与传统超声检测要求截然不同的全新的评定和验 查。仪器调试程序繁复，检测劳动强度大，周期长；