Sb含量对Mg-6Zn-Y-Zr-xSb合金组织与性能的影响.pdfVIP

Available online at _- Transactions of -;;- ScienceDirect Nonferrous Metals Society of China Trans. Nonferrous Met. Soc. China 21 (20 11) s222-s228 WWW. Effects of Sb content on microstructure and mechanical properties of Mg-6Zn-Y-Zr-xSb alloy l l l ZOU Chun-mingl.2.3 , ZHANG Yu-min2 , WANG Wei , WANG Hong-wei , WEI Zu时ie ， FU Bin-guol 1. School ofMaterials Science and Engineering , Harbin Institute ofTechnology, Harbin 150001 , China; 2. Center for Composite Materials , Harbin Institute ofTechnology, Harbin 150001 , China; 3. Key Laboraωry of Bionic Engineering of Ministry of Education, Jilin Univ町sity， Changchun 130025, China Received 10 May 2011; acc叩，ted 25 July 2011 Abstract: Effects ofSb content on microstructure and mechanical properties ofMg-6Zn-Y-Zr-xSb alloy were investigated by OM, SEM, XRD and mechanical prop衍ty test. The results indicate that addition of Sb can break continuous network structure inω partic1es in the interdendritic spaces, and with increasing Sb content, the volume 企action of these particles increases. The as-cast microstructure of the alloy with low content of Sb consists ofα-Mg， Zn-rich phase , eutectic structure (α-Mg+l-pha