聚氨酯对菱镁材料力学性能影响研究.doc

聚氨酯对菱镁材料力学性能影响研究 摘要：50年代末和70年代期间，菱镁制品在建筑工业中应用广泛，但是由于其制品的耐水性，强度等方面存在不足从而限制了菱镁制品在建筑工业中的推广和使用，到了近期，我国在菱镁制品的技术方面已有多年技术积累，已解决了几个技术关键，本文通过在菱镁材料中添加聚氨酯配制成的复合改性剂，采用实验的方法找出复合改性剂的最佳配方。加入复合改性剂后，菱镁制品的抗折、抗压和抗冲击性能都有很大的提高。 关键词：聚氨酯 菱镁材料 力学性能 Mechanical properties of polyurethane material impact on the study of magnesite Abstract: The late 1950s and 1970s， magnesite products are widely used in the construction industry， but because of its products， water resistance， strength， etc. to the deficiencies which limit the magnesium products in the construction industry in the promotion and use， to the recent China magnesite products in the technical aspects of many years of accumulated technology， has solved several key technology， this article by adding magnesium material polyurethane preparation of compound modifiers， using the experimental method to identify the most compound modifiers good formula. After adding compound modifier， magnesite products， bending， compression and impact resistance are greatly improved. Keywords: mechanical properties of glass fiber magnesite聚氨酯聚氨酯浓度对菱镁材料的复合材料力学性能的影响 序号 聚氨酯 浓度 拉伸强度/ MPa ( 气硬28 d) 拉伸模量/104MPa ( 气硬28 d) 弯曲强度/MPa ( 气硬28 d) 弯曲模量/104MPa ( 气硬28 d) 压缩模量/104MPa ( 气硬28 d) 冲击强度/ KJ·M-2 ( 气硬28 d) 1 0 78 2.1 100 2.3 2.0 12 2 1.0 95 2.2 125 2.4 2.1 13 3 1.5 101 2.3 144 2.5 2.2 14 4 2.0 126 2.4 167 2.6 2.3 15 5 2.5 135 2.4 185 2.7 2.3 15 6 3.0 150 2.5 200 2.9 2.4 16 由表1可知，当聚氨酯浓度为由0慢慢加到3.0的时候，拉伸强度由78 Mpa达到150 Mpa，拉伸模量由2.1×104Mpa达到2.5×104Mpa，弯曲强度由100 Mpa达到200 Mpa，弯曲模量由2.3×104Mpa达到2.9×104Mpa，压缩模量由2.0×104Mp达到2.4×104Mp，冲击强度由12 KJ·M-2 达到16 KJ·M-2。各项指标达到预期目标。 2.3.2　菱苦土细度对复合材料力学性能的影响 表2　磨细菱镁粉复合材料力学性能 序号 磨细时间/ h 拉伸强度/ MPa ( 气硬28 d) 弯曲强度/MPa ( 气硬28 d) 冲击强度/ KJ·M-2 ( 气硬28 d) 1 0 78 100 12 2 0.5 98 115 12 3 1 106 135 13 4 2 115 150 14 5 3 123 169 15 6 4 137 178 15 7 5 150 200 16 注: 上表试样玻纤质量分数为10%， 菱镁粉1 000 g， 卤水密度1. 27 g / cm3， 体积450 m L。 从图1、图2 可看出， 随着磨细时间的延长， 菱镁粉比表面积、标稠需水量等物理特性有较大的变化。菱镁粉磨细的结果， 打碎了粗大的粒子， 使其比表面积增大， 特别是初始3 h 内， 比表面积增大较快， 3 h