标准大全（The standard of）.doc

标准大全（The standard of）The tensile strength sigma b (MPa) is greater than 520, the yield strength is greater than 205, the elongation of delta 5 (%) is greater than 40, and the area of the cross section is equal to 60, hardness: less than or equal to 187HB. 90 HRB or less; 200 hv or less00 cr17ni14mo2 stainless steel (316 l)The low carbon steel of 0Cr17Ni12Mo2 is briefly introduced, which is more corrosive than the 0Cr17Ni12Mo2.00Cr17Ni14Mo2 (316L) stainless steel details stainless steel: 00Cr17Ni14Mo2 standard: GB/T 1220-1992Characteristics and scope of application: low carbon steel for 0Cr17Ni12Mo2, better than 0 cr17ni12mo2.Chemical composition:Carbon C: 0.030 or lessSi Si: 1.00 or lessManganese Mn: 2.00 or lessS: sulfur 0.030 or lessP P: 0.035 or lessCr: 16.00 ~ 18.00Ni: 12.00 ~ 15.00Molybdenum Mo: 2.00 ~ 3.00Mechanical properties:Tensile strength sigma b (MPa) : greater than 480Conditions yield strength sigma 0.2 (MPa) : greater than or equal to 177Elongation delta 5 (%) : is greater than or equal to 40The cross section shrinkage is psi (%) : greater than or equal to 60Hardness: 187 hb or less; 90 HRB or less; 200 hv or lessLow heat treatment specification and metallographic organization: heat treatment specification: solid solution of 1010 ~ 1150 ℃ cold fast. Metallographic tissue: the organization features the austenian body.Delivery status: generally delivered in heat treatment, the type of heat treatment is indicated in the contract; Unstated, delivered without heat treatmentHg20592-20635 flange standardHg20603-97 steel tube flange technical conditions20 # steel tubeDeviation level standard deviation toleranceD1 plus or minus 1.5%, minimum plus or minus 0.75mmD2 plus or minus 1.0%. Minimum + / - 0.50 mmD3 plus or minus 0.75%. Minimum plus or minus 0.30mmD4 + / - 0.50%. Minimum + / - 0.10 mmProject USESMeasurement of the THICKNESS GAUGE/UTG - 0 steel plateFlange is the national standard GB, crown crown SH is petrochemical industry standard, HGJ is chemical con