混合砂掺配比例理论分析.docVIP

混合砂掺配比例理论分析摘 要:由于机制砂和天然砂特性的不确定性,二者的掺配比例是决定混合砂技术特性的关键问题。基于技术参数分析,提出了混合砂掺配比例的计算方法。按照本方法确定的比例掺配得到的混合砂颗粒级配良好、粗细适中,符合《普通混凝土用砂、石质量及检验方法标准》(JGJ 52-2006)的技术要求。 关键词:人工砂;混合砂;掺配比例;颗粒级配 MIXING RATION OF MIXED SAND WITH THE THEORETICAL ANALYSIS ZHANG Xian?jiang (Huzhou Vocational Technical Education,Zhejiang Huzhou 313000,China) Abstract: As the characteristics of artificial sand and natural sand uncertainty, the mixing ratio of the two is the key issues to determine the technical characteristics of mixed sand. Based on technical data analysis,proposed a method of mixing ratio of mixed sand. In accordance with the method ofmixing the mixed sand are a good size distribution, thickness medium and consistent with the technical requirements of “Standard for technical requirements and test method of sand and crushed stone(or graved)for ordinary concrete “ (JGJ 52-2006). Keywords:artificial sand; mixed sand; mixing ratio; particle size distribution 1 引 言 随着我过基本建设规模的日益扩大,不少地区出现天然砂资源逐步减少,甚至无天然砂可用的情况。为适应新形势的发展,2002年2月1日起实施《建筑用砂》(GB/T 14684-2001)新标准,首次增加了人工砂种类,明确了人工砂中的混合砂品种。 国标实施后,人工砂在全国得到迅速发展。在工程实践中,用人工砂已配制出从 C??10?～C??70?的普通混凝土和泵送混凝土。在试验室设计强度 C100 的人工砂混凝土,90?d实际强度达到155?MPa[1]。人工砂已广泛应用于混凝土结构、砂浆和制品中。 就目前的状况而言,人工砂的工程应用超前于对人工砂本身的研究,而人工砂本身的特性最终决定混凝土或砂浆的物理力学性能。因此,对人工砂特性的深入研究是提高工程质量的基础性工作。 2 混合砂掺配比例的意义 2007年6月1日起实施的《普通混凝土用砂、石质量及检验方法标准》(JGJ 52-2006),提出的人工砂砂定义为:岩石经除土开采、机械破碎、筛分而成的,公称粒径小于5.00?mm的岩石颗粒,也即《建筑用砂》(GB/T 14684-2001)中所说的机制砂。混合砂定义为:由天然砂与人工砂按一定比例组合而成的砂。 我国人工砂生产主要有两种形式,一种是专门生产的机制砂,其级配细度模数均可做到优于天然砂,但其生产成本较高。另一种是生产碎石后的石屑经过简单加工和筛分或直接利用,这是目前人工砂的主体。其颗粒粒形呈三角形或方矩体,表面粗糙,棱角尖锐,有的片状颗粒较多,细度模数在2.6～4.0之间,大多偏粗,级配不良,含有5 %～18 %的石粉,其表面积比天然砂要大很多[2]。由于全国各地生产机制砂的矿源、加工设备和工艺不同 , 生产出机制砂的粒型和级配可能会有较大差别。 天然砂是指由自然风化、水流搬运和分选、堆积形成的粒径小于4.75?mm 的岩石颗粒。天然砂是一种地方性资源,由于受自然形成条件的限制,使其在技术参数、质量等级等诸多方面具有明显的地域性。 单独使用机制砂配制混凝土,因其表面粗糙,多棱角,且机制砂大多颗粒偏粗,级配较差,使混凝土拌合物和易性差,施工困难;单独使用天然细砂,由于其细度模数低,收缩大,易引起混凝土开裂[3]。将人工砂和天然细砂按一定比例配合而成的混合砂,用于高性能混凝土中,可减少水泥与用水量,节约成本,提高混凝土的经济性和耐久性人[4]。但是,由于人工砂和天然砂特性的不确定性,在