铝合金状态代号（Aluminum alloy status symbol）.docVIP

铝合金状态代号（Aluminum alloy status symbol） Basic status of alloy: F free processing state is applicable to the products with special requirements for processing hardening and heat treatment conditions during the forming process. The mechanical properties of the state products are not specified (unusual). O annealing status is applicable to processing products with minimum strength after complete annealing (occasionally appearing) H work hardening state Apply to improve strength by work hardening products, product after work hardening can pass (also (without) the strength decreases the additional heat treatment (usually as a heat treatment to strengthen material) W solid melting heat treatment state A state of instability, apply only after solution heat treatment, natural aging of the alloy at room temperature, the state only that products are in a natural aging phase (less common) T heat treatment condition (different from F, O, H state) is applicable to the stable product after heat treatment, after (or not). T code behind must have one or more with Arabic numerals (general type for heat treatment of intensive material) we common non heat treatment to strengthen the back of the aluminum alloy status code is commonly letter H add two Numbers. Such as 1100 H14. The following is a brief description of the following status codes. The letter H is followed by two Numbers: the first digit is the method of processing hardening treatment. The first number behind H is: 1, 2, 3, 4 That is, H1 * H1 * means simple process hardening treatment H2 * H2 * indicates process hardening and incomplete annealing H3 * H3 * represents processing hardening and stabilization processing H4 * H4 * indicates processing hardening and painting treatment The second number represents the degree of hardening the material has reached. The second number behind H is: 1, 2, 3, 4, 5, 6, 7, 8, 9 The hardness between H * 1 and 2 H * 2 1/4 hard The hardness between H * 3 2 and 4 The hardness of H * 4 1/2 hard H