新型水溶性半无机硅钢片漆的研制.pdfVIP

2008．41(1 赵 蕾等：新型水溶性半无机硅钢片漆的研制 1 新型水溶性半无机硅钢片漆的研制 赵 蕾 ，吴化军 ，罗翠锐 ，刘立柱 (1．哈尔滨理工大学 材料科学与工程学院，哈尔滨 150040； 2。嘉兴市清河高力绝缘有限公司，浙江 嘉兴 314031) 摘要：为了增大电机铁芯叠片间的绝缘，以改型酚醛树脂为基体，纳米TiOz为无机填料，研制了一种新型的水溶 性半无机硅钢片漆。实验结果表明，该漆不仅在力学性能和电学性能等方面达到了同外同类硅钢片漆的水平，而 且耐热性能优异，初始分解温度为392．632℃，优于进口漆的305．014℃，并且具有优良的储存稳定性。 关键词；水溶性；半无机；硅钢片漆 中图分类号：TM215．42 文献标志码：A 文章编号：1009—9239(2008)01—0001—03 A New Type of Water-soluble Semi—inorganic Varnish for Silicon Steel Sheet ZHA0 Lei 1 WU Hua-jun 2 LUO Cui．rui 1，LIU Li．zhu (I。School of Material Science Engineering，Harbin University of Science and Technology,Harbin l5oo40．China；2．Jiaxing Qinghe Gaoli Insulated Material Co．．Ltdt Jiaxing 314031，China Abstract：A new type of water—soluble semi-inorganic silicon steel sheet varnish was developed for en- hancing the insulation between silicon steel sheets which were used in electric motors．The matrix of the varnish is modified phenolic resin and the inorganic filler is nano．Ti02．The test results show that the mechanical and electrical properties of the varnish are as fine as that of the same type of imported varnish．The initial decomposition temperature of the varnish is 392．632℃．which is higher than that of the imported varnish．305．014℃ ．Furthermore the new varnish is in the nature of superior storage stability． Key words：water—soluble：semi-inorganic；steel sheet varnish 1 前 言 无机硅钢片漆成为研究的热点。 能源是21世纪四大支柱产业之一，目前由于能 我国该项技术的研究起步较晚，落后于世界先进 耗的迅速增加，降低电能消耗已成为当今世界面临的 水平，经过近二十年的发展，取得了一定的进步，先后 重大课题。因此，对具有非常低的铁损和高磁导率的 有多种硅钢片漆研制成功，但多数为传统的溶剂型有 高效铁芯材料的需求量不断增加。无取向硅钢是广 机硅钢片漆，水溶性半无机硅钢片漆数量不多，而且 泛用作旋转机器和静电机器的铁芯材料。随着电机单 与进口水溶性半无机硅钢片漆相比，国产水溶性半无 机容量的不断增大和电机、电器的耐热等级的提高，