NiO活性对高频低磁导率NiCuZn铁氧体Q值的影响 Effect of NiO Activity on the Q Value of High Frequency and Low Permeability NiCuZn Ferrite.pdfVIP

王勤峰，白本帅 (天通控股股份有限公司，浙江海宁314412) 摘要：以不同工艺生产的NiO为原材料，制备了高频低磁导率NiCuZn铁氧体．用扫描电镜(SEM)分 析原材料NiO的微观形态的差异，用x射线衍射(XRD)研究预烧后固相反应的进行状况，考察了不同NiO 材料对低温烧结材料高频Q值的影响．研究发现，低温烧结条件下，高活性的NiO原材料能有效提高低磁导率 NiCuZn铁氧体的高频Q值． 关键词：NiCuZn铁氧体：NiO活性；固相反应；Q值 中图分类号：TM277+．1 文献标识码：B 文章编号：1001．3830(72008)05．0051．02 ’ ＼ EffectofNiO ontheValueof ActivityQ HighFrequency andLow NiCuZnFerrite Permeability WANG Ben—shuai Qin-feng，BAI TDG 314412,China HoldingCo．，Ltd,Haining NiCuZnwere different microstructuresof Abstract：Theferrites NiO preparedusingproducedby process．111e lawmaterialsNiOwere SEM．ThesolidstatereactionwereresearchedXRD．TheinfluenceofNiO investigatedby by lawmaterialsonthe factorat oftheferritesinteredatlow werestudied．ItWSS qualityQ highfrequency temperature to of foundthatthe NiOcontributedtheincreaseof valueat lowinitial highactivity Q highfrequency permeability NiCuZnferrite． words：NiCuzn state value Key ferrite；NiOactivity：solidreaction；Q 片式电感器的低温烧结NiCu2rn铁氧体材料的开发 1引言 有很大借鉴作用。 低磁导率的镍系铁氧体特别是起始磁导率为 本研究通过采用高活性NiO原材料，使烧结 15、使用频率在120MHz的材料，一般都采用富铁 温度降低到950℃，消除大量助熔剂加入的不利影 配方【l】。由于富铁配方的镍系铁氧体没有加入CuO 响，并制备出了性能优良的高频低磁导率的高Q 等助熔剂，材料的烧结温度一般都在1200℃左右， 值NiCuZn铁氧体材料。 甚至达到1300℃，对生产的烧结设备要求较高且