Corrosion and Hardness Behaviour of AISI 316L （腐蚀和硬度的行为符合美国钢铁协会的316 l）.pdfVIP

Corrosion and Hardness Behaviour of AISI 316L SS Implanted with Argon and Oxygen Ions Korózne a pevnostné vlastnosti AISI 316L SS pri implantácii iónmi argónu a kyslíka V. Muthukumaran, V. Selladurai, S. Nandhakumar, M. Senthilkumar Abstract 1 Introduction Ion implantation creates alterations in surface properties In the recent years, many attempts have been made to of solids such as corrosion and hardness. The AISI316L improve the surface properties of metals and alloys used in stainless steel is being widely used both in artificial knee biomedical applications [1].Ion implantation is a high end and hip joints in bio-medical applications. In the present technology adopted specifically for modifying surface study, the AISI316L SS was implanted with two different properties of materials. Though it is similar to the coating ions namely argon and oxygen separately at 100 KeV with a process, it does not involve the addition of a layer on the dose of 1x1017ions/cm² at the temperature of 32°C. The surface. Importantly ion implantation serves as a powerful crystallographic orientation and surface morphology were tool of surface engineering of biomaterials. The main ad- studied using X-ray Diffraction (XRD) and Scanning vantages of this technique are the possibility of introducing Electron Microscope (SEM). The effects of ion implantation any element into any solid target and the low temperature of on the corrosion performance of AISI316L stai