铝合金状态代号（Aluminum Alloy state code）.docVIP

铝合金状态代号（Aluminum Alloy state code） Alloy basic state code: F free state for processing in the molding process, work hardening and heat treatment conditions for the special requirements of the product, the mechanical properties of the products are not specified (not common) O which is suitable for processing products in the annealed state completely annealing was the lowest strength (occasionally) H hardening condition applied to improve the strength of the product through the hardening product in hardening after after (or not after) additional heat treatment. The strength decreased (the general non material heat treatment) W solid solution heat treatment state of an unstable state, applies only after solution heat treatment, natural ageing alloy at room temperature, the state code said only products in the natural aging stage (less common) T heat treatment (F, O, H in different states) is suitable for heat treatment, with (or without) hardening to achieve stable products. The T code must be followed by one or more digital (Arabia general heat treatment strengthening materials) our common non heat treatment strengthening type code behind Aluminum Alloy is generally H with two digits. Such as 1100 H14. The meaning below introduces the following status code. After the letter H with two digits: work hardening processing method is the first digital representation. The first digit behind the H are: 1, 2, 3, 4 H1* H1* said the simple hardening treatment H2* H2* said the work hardening and incomplete annealing H3* H3* said the hardening and stable machining processing H4* H4* said the work hardening and coating processing The hardening degree reached second digits is material. Following the H second digits: 1, 2, 3, 4, 5, 6, 7, 8, 9 H*1 is between 0 and 2 the hardness H*2 1/4 hard The hardness of H*3 between 2 and 4 H*4 1/2 hard H*5 hardness of between 4 and 6. H*6 3/4 hard H*7 hardness of between 6 and 8. H*8 H*9 super hard hard state state Not many H followed three number