面板混凝土抗裂效能试验探究.docVIP

面板混凝土抗裂效能试验探究【摘要】 混凝土在约束状态下早期抗裂性能的试验方法，国内外研究综合起来分为三大类：平板法、圆环法和棱柱体法。本文结合青海黄南州扎毛水库工程，按照CECS13:2009《纤维混凝土试验方法标准》中“早龄期抗裂性对比试验”方法进行抗裂效能试验。通过采用四边约束的薄板模拟工程中钢筋限制混凝土的状态，反映收缩裂缝的形态及不同纤维掺量对混凝土的阻裂效果，同时为施工中预防混凝土早期裂缝提出措施供参考。 【关键词】混凝土； 抗裂效能； 试验 【 abstract 】 the constraint condition of concrete crack resistance of the early testing method, the domestic and foreign research comprehensive up into three types: flat method, circle method and the prism body method. This paper point in qinghai plunge hair reservoir project, according to the CECS13:2009 “fiber reinforced concrete test method standard” in “early age resistance to contrast test” method of crack performance test. Through the use of four constraints sheet of reinforcement in concrete engineering simulation limit state, reflect the shrinkage crack of morphological and different fiber contents of the resistance of concrete crack effect, at the same time for construction of the early concrete crack prevention measures put forward for reference. 【 keywords 】 concrete; Crack performance; test 中图分类号：TU37文献标识码：A 文章编号： 0前言 混凝土面板堆石坝由于理论上“自身安全”的特点而具有较高的安全储备，现已成为世界上公认的一种比较经济适用的坝型，它是用堆石或砂砾石分层碾压填筑成坝体，并用混凝土面板作防渗体。 黄南藏族自治州位于青海省东南部，属高原亚寒带大陆性气候，气温较低，热量不足。年平均气温4～8℃，≥10℃的持续天气只有120～160天。夏季短促温凉，冬季漫长寒冷。扎毛水库总库容为4350万立方米，后式电站装机7500千瓦，年平均发电量3543万千瓦时。设计最大坝高74m，坝顶长度291.63m，坝顶宽7m，上游坝坡1:1.5，下游坝坡1：1.25，面板厚度为30～50cm。根据设计说明和当地环境条件，按照防冻、防裂的思路研究了该水库坝体面板混凝土配合比，并采用薄板进行混凝土抗裂效能试验，通过分析不同纤维掺量的抗裂性能，一方面验证纤维掺量的合理性，另一方面提出预防混凝土早期裂缝措施。 1扎毛水库面板坝面板混凝土要求 根据设计文件要求，青海黄南州扎毛水库面板混凝土的设计强度等级为C30；该区段常年气温较低，规定混凝土抗冻等级为F300；另外，为防止面板开裂和渗漏，对抗裂性和抗渗性也做了较高的要求。混凝土性能指标及技术要求如表1所示。 表1混凝土主要性能指标及技术要求 2 面板混凝土配合比 2.1原材料 水泥：采用祁连山P.O42.5水泥,检验结果均满足《通用硅酸盐水泥》（GB175-2007）规范要求。28d抗压强度52.8MPa、抗折强度7.5 MPa；粉煤灰：采用甘肃全鑫F类Ⅱ级粉煤灰，检验各项指标均满足《水工混凝土掺用粉煤灰技术规范》（DL/T5055-2007）中F类Ⅱ级粉煤灰技术要求，细度21%，需水量比100%；细骨料和粗骨料：采用隆务河上游砂石料厂生产的天然河砂和卵石粗骨料，检验结果均满足《水工混凝土施工规范》DL/T 5144-2001中细骨料和粗骨料品质要求，其中砂细度模数为2.80，粗骨料为连续级配比例为5～20mm:20～40mm=60%:40%；外加剂：采用江苏博特JM-PCA(Ⅳ)聚羧酸减缩抗裂减水剂和GYQ(Ⅰ)高效引气剂，检验结果均满足《混凝土外