论述超声波探伤在钢结构焊缝中应用.docVIP

论述超声波探伤在钢结构焊缝中应用摘要：超声波检测是常规的无损检测方法之一。随着国内钢结构多层建筑的不断增多，无损检测工作量也越来越大，除了在焊接工艺上加大控制以外在无损检测上也应加大检测力度，并应尽早在钢结构高层建筑焊缝无损检测标准上体现出来。本文就是基于此，进行了超声波探伤在建筑钢结构焊缝中的运用的相关探讨的。 关键词：无损探伤技术；超声波探伤；高层建筑 Abstract: ultrasonic detection is one of the normal NDT methods. With domestic steel structure of multi-storey building is on the increase, nondestructive testing is more and more big workload, except in welding technology to increase control in the outside nondestructive testing should be increased detection dynamics, and should soon in steel structure high-rise building weld nondestructive testing standards reflected. This paper is based on this, the ultrasonic inspection in construction steel structure of the use of the weld the relevant discussion. Keywords: NDT technology; Ultrasonic inspection; High-rise building 中图分类号：[TU208.3]文献标识码：A 文章编号： 一、钢结构焊缝无损探伤技术 钢结构在大型厂房、桥梁、多层建筑等都有着广泛的应用。为确保工程质量必须对钢结构焊缝进行无损探伤。钢结构焊缝无损探伤技术主要有超声波探伤、射线探伤以及磁粉探伤。超声波探伤是目前应用最广泛的无损探伤方法之一，该法采用高频超声波穿过被检焊缝，当遇到缺陷时超声波反射，通过反射波的幅度和位置判断缺陷性质、位置及大小。射线探伤技术是采用X射线透照被检焊缝，焊缝内部的缺陷对X射线的反射、吸收使之在底片上留下影像，通过底片上的影像即可判断焊缝内部缺陷。磁粉探伤技术是一种表面探伤技术，其原理是材料或焊缝表面缺陷造成表面材质的不连续，当外加磁场在该处时，其表面磁场分布与无缺陷处不同，利用磁粉指示出磁场分布，即可判断材料或焊缝的表面缺陷。 二、超声波探伤的基本原理 钢材原材料缺陷可以采用平探头纵波探伤，探头轴线与其端面垂直，超声波与探头端面 或钢材表面成垂直方向传播；超声波通过钢材上表面、缺陷及底面时，均有部分超声波反射回来，这些超声波各自往返的路程不同，回到探头的时间不同，在示波器上将分别显示出反射脉冲，分别称其为始脉冲、伤脉冲和底脉冲。当钢材中无缺陷时，则无伤脉冲。始脉冲、伤脉冲和底脉冲波之间的间距比等于钢材中上表面、缺陷处和底面的间距比，由此可确定出缺陷的位置。焊缝探伤主要采用斜探头横波探伤，斜探头使声束斜向人射，斜探头的倾斜角有多种，使用斜探头发现焊缝中的缺陷与用直探头探伤一样，都是根据在始脉冲与底脉冲之间是否存在伤脉冲来判断。当发现焊缝中存在缺陷之后，根据探头在试件上的位置以及缺陷回波在显示屏上的高度，就可确定出焊缝的缺陷位置和大小。这是因为在探伤前按一定的比例在超声仪荧光屏上作有距离——波幅曲线。 三、高层建筑钢结构焊缝超声波 高层建筑由于集中了当今世界上众多方面的高新技术，其技术含量高，又充分显示了当代建筑业的最高水平，且其占地面积小，在大城市的黄金地段就有了很强的竞争力，当然，事物是一分为二的，高层建筑也不可避免地存在着缺点和不足，其中之一是抗震性能差，防震要求高。为了提高高层建筑的抗震性能，就出现了钢结构的高层建筑，就有了承受高强度的钢焊缝，就需要对这样的焊缝进行严格的超声波探伤。钢结构高层建筑的基本单元是柱和梁。当前钢结构的柱、梁连结大多用焊缝加高强螺旋的方法，也就是在柱、梁的复板(立板)上用高强螺旋连结，而在翼板(面板)上用焊缝连结。这样就充分发挥了高强螺旋和焊缝的各自优点、又便于工地现场高空吊装时的定位和装配。常见的柱有H型柱(大规格的H型型钢制作)、箱形柱(由厚钢板拼装制作)和圆形桂(由大厚度铸钢离心铸造制作)。桂与柱都是由对接焊缝连接成一体，梁都是由H型型钢制成的，称H梁。 四