浅议水利施工中混凝土裂缝产生分类-原因及处理方式.docVIP

浅议水利施工中混凝土裂缝产生分类\原因及处理方式摘要：凝土是一种由砂石骨料、水泥、水及其他外加材料混合而形成的非均质的多项复合脆性材料。由于混凝土施工和本身变形和约束等一系列问题，使混凝土产生裂缝，微裂缝通常是一种无害裂缝，对混凝土结构的承重、防渗及其他功能不产生危害。严重的将直接威胁到人民的生命、财产安全。因此对混凝土裂缝的控制已成为水利工程建设引起高度重视的问题之一。严重影响到水利工程的整体建筑使用及工程的质量。对大体积混凝土裂缝进行分类，分析了其形成的原因，并围绕如何避免裂缝的产生提出一些控制措施。 关键字：水利工程，混凝土，裂缝，施工 Abstract: soil is a kind of by sand aggregate, cement, water and other plus material mixed, in the form of inhomogeneous many composite brittle material. Because of the concrete construction and itself deformation and restraint and so on a series of problems, make the cracking of concrete micro cracks is usually a harmless cracks of concrete structure bearing, seepage control and other functions do not produce harm. Serious will be a direct threat to people’s life and property security. So the concrete cracking control has become the attention water conservancy construction part of the problem. The serious influence to the whole of the water conservancy project construction use and the quality of the construction. For mass concrete crack classification, analyses the reasons, and focus on how to avoid the cracking of the proposed some control measures. Key word: water conservancy works, concrete, crack, the construction 中图分类号：TV文献标识码：A 文章编号： 一、水工混凝土裂缝的分类 1收缩裂缝 （1）表面裂缝，大体积混凝土的内部热量向外散发的较慢，而其外表面与外界接触温度散热速度较快，由于其内部和表面的散热速率不一样，在混凝土的表面会产生一种温度梯度，引发表面产生拉应力，内部产生压应力；如果温差产生的表面拉应力超过此时的混凝土极限抗拉强度，就会在混凝土表面产生裂缝，一般出现在混凝土浇筑后的第3-4天。 （2）贯穿裂缝，混凝土在浇筑数天后由于逐渐降温而产生收缩，再加上混凝土硬化过程中拌合水的水化以及胶质体的胶凝等作用，使得混凝土结构开始收缩，由于受到基底或结构本身的约束，也会产生拉应力，当此拉应力超过混凝土此时的极限抗拉强度，在混凝土结构的薄弱区域就可能产生贯穿裂缝，这种收缩裂缝危害较大。 2塑性塌落裂缝 在混凝土浇筑过程中或者在浇筑初步成型时，都会产生一种塑性塌落裂缝。因为在混凝土的成型过程中，其拌合物中的骨料缓慢下沉，水向上浮，此时钢筋上面的混凝土被钢筋支顶，而钢筋两侧及其下方的混凝土产生下沉，导致混凝土沿钢筋表面产生顺筋裂缝。 3水化热裂缝 水化热裂缝多在大体积混凝土中发生。由于混凝土水化热过高，在凝固过程中释放出大量的水化热，致使混凝土内部温度与混凝土表面温度以及外部环境的温度相差较大，加之有结构自身约束存在，从而产生温度和收缩应力，导致水化热裂缝的产生。通常情况下，大体积混凝土当混凝土内部与表面温度超过24℃，混凝土表面温度与环境温度超过15℃时，最高浇筑温度大于27℃时，则易出现水化热裂缝。 4干缩裂缝 该裂缝多出现在混凝土硬化过程中。由于混凝土失水后干燥，引起体积收缩变形，这种体积变形受到约束时，就可能产生干缩裂缝。混凝土干缩裂缝，一般有三种形状：不规则龟纹状或放射状