可塑纤维桩全瓷冠在上前牙美学修复中应用探析[摘要]目的:探讨上前牙残冠残根或前突错位的理想修复方法。方法:用everStick高强度纤维桩加In-Ceram渗透氧化铝全瓷冠对59例(96颗)须行桩冠修复的上前牙进行美容修复,追踪观察1～4年。结果:除1例(单颗)侧切牙在修复第3年出现破裂,其余修复体修复效果良好,未见根折及崩瓷。结论:everStick高强度纤维桩及氧化铝全瓷冠是上前牙美学修复的理想方法。 [关键词]高强度纤维桩;氧化铝全瓷冠;上前牙美学修复 [中图分类号]R783 [文献标识码]A [文章编号]1008-6455(2010)07-1020-02 Application discussion of everStick fiber resin post-core and all ceramic crown in aesthetics restoration of maxillary labial teeth PENG Li-hui,ZHONG Ai-xi,PAN Xiao-Bo,LIU Guang-xue,LI Rong-ting (Department of Stomatology,People’s Hospital of Guangxi Zhuang Autonomons Region,Nanning 530021,Guangxi,China) Abstract:ObjectiveTo discuss ideal prosthetic method af maxillary labial teeth being residual root,trusion or protrusion. Methods 96 maxillary labial teeth needed aesthetics restoration of post-core and crown were restored with everStick fiber posts andIn-Ceram alumina base all ceramic crown,and fallowed up 1 to 4 years.Results 95 crows were sealed and had good retentive power, without crown or root fracture,1 crow was fracture after 3 years.Conclusion The ideal prasthetis method of maxillary labial teeth is ever Stick fiber risin post-core and In-Ceram alumina bass all ceramic crown.Aesthetics restoration of maxillary labial teeth Key words:high-strength glass fibers post;inceram alumina bass all ceramic crown;aesthetics restoration of maxillary labial teeth 桩冠修复是上前牙残根、残冠或错位、前突的常用的美学修复方法之一。目前,常用的铸造金属桩核及金属烤瓷冠由于金属桩弹性模量较大,易导致根折,金属底层冠的不透光性、氧化层渗透等影响了修复体的美学性能,难以满足患者日益提高的美学要求。近年来,笔者采用高强度的可塑纤维桩核+氧化铝全瓷冠对残根残冠或错位、前突的上前牙进行修复,效果良好,患者满意。现报道如下。 1资料和方法 1.1病例选择:2006年3月～2009年1月选择到我科就诊的上前牙需要修复的患者59例(96颗),其中男性21例(30颗),女性38例(66颗),年龄19～50岁。纳入标准:①均为上前牙残根残冠无法单纯充填治疗,须做桩冠修复;②上前牙错位或前突的患者已到口腔正畸科就诊并拒绝采用正畸方法矫正,而选择修复方法;③牙根无松动,无根折;④均已进行完善的根管治疗,术后X线片示根充适填、密合。 1.2 材料:1.2mm、1.6mm,everStick高强度纤维(芬兰),瑞士产Parapost Cement纤维套装(包括根管内处理剂,桩根内粘固剂,酸蚀剂、桩核树脂及桩核成形塑料套),In-Coram渗透氧化铝全瓷系统(Vita公司,德国)。 1.3 操作步骤:①常规根面预备:在尽量保存牙体组织的前提下,在基牙唇侧制备出0.8～1mm的唇侧颈缘肩台于龈下0.5～1mm处,依据上下前牙的咬合关系磨除舌侧牙体组织,近远中及舌侧颈缘均应制备肩台于龈下