characterization of ceramic filled polymer matrix composite used for biomedical applications表征陶瓷填充聚合物基复合材料用于生物医学应用.pdfVIP

Journal of Minerals Materials Characterization Engineering, Vol. 10, No.12, pp.1167-1178, 2011 Printed in the USA. All rights reserved Characterization of Ceramic Filled Polymer Matrix Composite Used for Biomedical Applications 1* 2 3 Waleed Asim Hanna , Faiza E. Gharib , Ismail Ibrahim Marhoon 1 Materials Engineering Department, University of Technology , Baghdad-Iraq. 2 Environmental Engineering Department, College of Engineering, Al-Mustansiriya University, Baghdad-Iraq . 3 Materials Engineering Department, College of Engineering, Al-Mustansiriya University, Baghdad-Iraq *Corresponding author: alnasir69@ ABSTRACT A particulate composite material was prepared by adding (CaCO , CaO, MgCO , MgO) ceramic 3 3 particles with particle size of ( 53 µm) to unsatu rated polyester resin with weight fraction of (3, 6, 9, 12, 15)% and fixed amount of CaF (0.5% wt.). The results had revealed that the maximum 2 values of tensile strength, compression, bending strength, hardness, impact energy and water absorption%, were (57.6828 N/mm2 at 3% wt. CaCO , 124.0965 N/mm2 at 9% wt. CaCO , 3 3 2 102.188 N/mm at 9% wt. MgO, 88.2 Shore D at 9% wt. CaCO , 0.27 J at 6%wt. CaCO and