T8钢锻后余热热处理研究.doc

T8钢锻后余热热处理研究 摘 要： 关键词：T8热处理锻后余热 T8 steel forging after heat treatment study of waste heat AbstractT8 steel is a kind of common steel industry. Beginning of T8 steel forging temperature about 1100 ℃, the final forging temperature about 850 ℃.because its cheap and source is easy, often used to do a simple mold, as and the low speed cutting tools, woodworking tools, chisels, chisel. T8 steel common heat treatment process is spheroidizing annealing, quenching and tempering. But the spheroidizing annealing time is too long. Because of this, heat treatment time is too long, and large energy consumption. This design mainly is the study of use of T8 steel high temperature after forging, heat treatment directly. Testing a use after forged heat treatment process of waste heat. So save energy, improve production efficiency. Keywords: T8,Heat treatment,Forging after heat 目 录 绪论 1 1热处理的概述 3 2 T8钢的特性及应用范围 4 2.1特性 4 2.2应用 4 2.3T8钢的化学成分（/%） 4 2.4 T8钢的物理性能 4 3 T8钢与其他碳素工具钢的对比 7 4钢的锻造温度 9 4.始锻温度 9 4.2终锻温度 9 4.3锻造温度范围 9 5 T8钢的普通热处理工艺 13 5.T8钢球化退火的目的及球化退火后的组织结构和性能 13 5. T8钢淬火的目的及淬火后的组织结构和性能 13 5.T8钢低温回火后的目的及回火后组织结构和性能 13 6普通热处理工艺对T8钢显微组织及硬度的影响 15 6.1 球化退火对组织的影响 15 6.2 淬火组织及硬度 16 6.3 回火组织及硬度 18 20 7.1T8钢锻后余热退火 20 7.2T8钢锻后余热退火的特点 20 7.3T8钢锻余热淬火工艺 20 20 8实验 23 8.1 实验方案 23 8.2硬度测试 23 8.3 抗拉强度 25 8.4冲击韧性 26 8.5实验结果 26 结论 28 参考文献 29 致 谢 30   绪论 在机械制造上T8钢得到非常广泛的应用，T8钢的含碳质量分数一般在百分之零点七五到百分之零点九零之间，经过普通热处理后硬度一般在60到63HRC之间。因为T8钢的热处理工艺简单并且生产成本也低。冷、热加工性能好,并且热处理之后的硬度和耐磨性都比较高，所以在机械行业中得到广泛应用。T8钢由于含碳量在百分之零点七五到百分之零点九零之间，热处理后因其碳化物过多所以T8钢的塑性和韧性都比较的差。如果采用的热处理工艺不合适，会使T8钢在使用早期出现开裂和破碎的现象。在实际产生中，T8钢经常用来做刀具，刀刃与工件在切削过程中由于较强摩擦会产生严重磨损以及大量热量，使刀刃温度升到600℃之上，甚至更高，很可能导致刀具崩刃或者折断现象，直接缩短了刃具的使用寿命。T8钢锻造加工后必须进行适当的球化处理，使T8钢中粒子和局部高碳地方形成碳化物核心使其聚集球化，同时细化铁基体晶粒度，再经过淬火回火，使大量弥散析出碳化物颗粒，阻碍奥氏体晶粒长大。我国很早便对T8钢进行研究分析。当前，T8钢件锻造后还是广泛采用球化退火工艺，锻后空冷后进行球化退火。 本课题以金属学与热处理方面的知识为基础，通过热处理工艺进行分析及相关参数的计算，进一步得出在锻造工艺结束时如何利用T8钢的终锻温度，在不加热的情况下制定相关热处理的工艺方案。总结出一定的规律及方法。 另外通过课题研究加深巩固已学知识。并且通过一定的实验提高学生动手实验能力以及提出问题分析问题解决问题