20钢热处理正火过程温度场分析.doc

20钢热处理正火过程温度场分析 摘 要：选取20钢为研究对象，利用ANSYS软件建立有限元模型，通过热分析模块对20钢正火过程温度场分布进行了模拟计算。结果表明随着逐渐的冷却，零件的温度迅速降低，零件的各个点温度下降的速率不同，而且随着冷却的时间越长，温度也随之越来越低。在空冷刚开始的时候，温度下降的速度较快，中心降温过程中受零件其他部分的热影响大，下降速度慢。 关键词：20钢；温度场；ANSYS模拟 Thermal analysis of Steel 20s normalizing heat-treatment Abstract：Select 20 steel as the research object, the finite element model is established by use of ANSYS software, and through the thermal analysis module of 20 steel normalizing process simulation on temperature field distribution. Results show that along with the gradually cooling, the temperature of the parts to reduce rapidly, each point temperature drop rate of different parts, and as the longer the cooling time, low temperature has been more and more. In air cooling in the beginning, the temperature drops faster, center by the rest of the parts in the process of cooling heat affected big, slow down. Keyword: steel 20；The temperature field；Ansys simulation 目 录 1 绪论 1 1.1 研究目的及意义 1 1.2 国内外研究进展 1 1.3 研究的主要内容 2 1.4 研究方法 3 2 20钢热处理工艺 4 2.1 20钢概述 4 2.2 热处理工艺的制定 5 3 ANSYS有限元软件 8 3.1 简介 8 3.1.1 热分析 9 3.2 主要模块介绍 9 3.3 有限元单元法概念 12 4 基于ansys正火过程温度模拟 13 4.1 温度场数学模型建立 13 4.2 相关数据确定 13 4.3 材料参数 14 4.4 前处理 15 4.5 施加载荷 17 4.6 求解及分析结果 17 4.6.1 正火过程某些时刻温度场分析 17 4.6.2 空冷过程某些特定点位置随时间变化曲线图 20 4.7 模拟结果分析 23 5 总结 24 5.1 展望 24 参考文献 25 致谢 27 1 绪论 1.1研究的目的及意义 20号钢是含碳量为0.2%的低碳钢，很少淬火，无回火脆性。切削加工性冷拔或正火状态较退火状态好、一般用于制造受力不大而韧性要求高的。优质低碳碳素钢，冷挤压、渗碳淬硬钢。该钢强度低，韧性、塑性和焊接性均好。抗拉强度为355500MPa，伸长率≥24%Ac3(Ac?是指加热时自由铁素体全部转变为奥氏体的终了温度)或Acm(Acm是实际加热中过共析钢完全奥氏体化的临界温度线以上30-50℃，保温一段时间后，从炉中取出在空气中或喷水、喷雾或吹风冷却的金属热处理工艺。其目的是获得一定的硬度、细化晶粒，并获得比较均匀的组织和性能[2]。 低碳钢正火的目的之一是为了提高切削性能。但是对有些碳的质量分数低于0.20%的钢，即使按通常正火温度正火后，自由铁素体量仍过多，硬度过低，切削性能仍然较差。为了适当提高硬度，应提高加热温度（可比Ac3高100℃），以增大过冷奥氏体的稳定性，而且应该增大冷却速度，以获得较细的珠光体和分散度较大的铁素体。 计算热处理正火过程某些时刻温度场的分布及某些特定位置温度随时间的变化关系，通过研究，让我更加了解20钢通过正火过程温度场分析的准确数据，更深的了解对20钢的认识。 1.2 国内外的研究进展 多年来20钢以其优良的性价比在石油化工等行业得到了更广泛的应用[3]，但在大型构件的实际生产中，有焊接过程复杂的温度变化所引起的焊接变形和残余应力往往影响结构的使用寿命，因此，对温度场的研究一直受到普遍重视。随着计算机技术的发展