一些常见混凝土裂缝成因和预防.docVIP

一些常见混凝土裂缝成因和预防 　　摘 要:随着社会不断的发展，建筑工程在人们的生活中占有举足轻重的作用，而砼在建设工程中占有很重要的地位，砼在结构安全、耐久性和工程造型等方面起着决定性的作用。根据本人多年在建筑工程技术管理中积累的工作实践,对建筑工程一些常见的砼裂缝的成因进行了分析，砼的裂缝是我们平时施工中最为普遍的质量通病，针对砼裂缝的成因从原材料、施工控制、地基变形、温度等四个方面探讨。 关键词:混凝土裂缝；成因；预防 Abstract: With the constant development of society, construction occupies the role play a decisive role in people’s life, and the concrete occupies a very important position in the construction engineering, concrete plays a decisive role in the structural safety, durability and other aspects. According to my many years of accumulated in the construction engineering management practice, the causes of some common concrete cracks in construction are analyzed, the concrete crack is usually the most common construction quality problems, the causes of concrete cracks from four aspects of raw material, construction control, foundation deformation, temperature and so on. Key words: concrete cracks; causes; prevention 中图分类号：TV543+.6文献标识码：A 文章编号：2095-2104（2013） 一、建筑工程混凝土裂缝产生的原因分析 （一） 砼原材料的质量缺陷导致裂缝 1．水泥为砼中的胶凝材料，水泥中含有生石灰或氧化镁等成分，这些成分和水接触后体积会膨胀，等水化热结束后体积又会收缩，易形成裂缝。 2．部分骨料中含碱率很高，与水泥会发生碱骨料反应，砼体积也会先膨胀后收缩，形成砼裂缝。在施工中沙、石的质量直接影响这砼的强度，如强度达不到要求砼可形成裂缝。 3．砼的拌制用水不得使用PH值小的酸性水和硫酸盐超过水重1%的水，如拌制水中含有其它化学成分及杂质会改变砼的质量及连锁反应，从而引起砼的裂缝。 4．现代砼施工中有很多外加剂能改善砼的性能和凝结时间，在实际采用外加剂时如不严格按照掺量使用就会影响砼的凝结时间及强度，从而改变砼的质量引起砼的裂缝。 （二）砼施工质量差导致裂缝 1．砼的配合比是决定砼强度等级的根本依据，砼抗压强度主要取决于水泥标号和水灰比，同样的配合比水泥标号越高则砼强度越高，反之越低。水灰比越大砼强度越低，反之越高。所以砼的配合比首先要依据设计强度找相关资质的实验室结合原材料实际情况进行试配，待砼强度等级、耐久性、坍落度符合普通《混凝土配合比实际规程》后方可使用。在实际拌制时严禁私自改变配合比。 2．在砼的浇筑前对有特殊要求、技术复杂、施工难度大的结构部位要编制专项施工方案，待监理工程师审核认可后实施，并以此方案认真检查落实到位。在砼的施工地点首先检查砼的坍落度对强度等级、坍落度和其它性能不符合要求的砼不得使用拌制砼时，试验人员要随机见证取样制作砼试块。 3．砼浇筑时要严格按照控制流程浇注，合理安徘施工顺序，砼振捣方法要正确不能有漏振或超振等情况发生。对已浇注的砼在终凝前应进行二次振捣提高粘结力和抗拉强度减少内部气孔提高抗裂性。 4．砼养护能保持水化热的温度和湿度，砼浇筑后要及时用塑料薄膜覆盖，待终凝后用湿润的草帘麻袋等覆盖并注意洒水养护延长养护时间。保温能减少砼表面的湿度及热量散失过快防止砼表层与内部温差较大时发生温度应力裂缝，在高温季节宜及时用塑料薄膜覆盖并用湿草袋覆盖砼保持湿度以免表面快速硬化后引起砼表面干缩裂缝，在寒冷季节砼表面因采取保温措施以防止冻裂缝。砼的施工质量控制是施工管理中的核心，施工质量的控制直接影响到砼强度、影响到工程质量，引起砼的裂缝。 （三）地基不均匀沉降导致裂缝 由于