预处理方式对橡胶混凝土硬化性能的影响.PDFVIP

预处理方式对橡胶混凝土硬化性能的影响 郭庆，马伍平 深圳市高新建混凝土有限公司 摘 要：为改善橡胶混凝土的力学性能，对橡胶颗粒进行NaOH溶液和酸性KMnO 溶4 液预处理，测试了橡胶混凝土的抗压强度，抗折强度及弹性模量，并利用SEM实验观察预 处理后橡胶集料表面形貌的变化。试验结果表明：橡胶预处理方式对混凝土的抗压强度和弹 性模量的影响较小，但对橡胶混凝土的抗折强度有明显的改善作用抗折强度最高提升了 20.7%。综合比较对各硬化性能的影响，酸性KMnO 的改善效果要优于NaOH预处理。4 关键词：橡胶混凝土；预处理；力学性能；微观形貌 中图分类号：TU528 文献标志码：A ExperimentalStudyonHardenPropertiesofRubberConcrete PretreatedbyDifferentWays Abstract: In order to improve mechanical properties of rubber concrete, rubber pretreated by NaOH solution and KMnO solution experiments were carried out. Effects of rubber pretreated 4 methodsanddosageonmechanicalpropertiesandYong’smoduluswereinvestigatedinthisstudy. SEMtests were carried outto studythe surface feature ofrubber particles.The results indicated that rubber after pretreatments can increase the flexural strength, but the improvement of compressive strengt and elastic modules were not efficiently.The effects of KMnO pretreated4 werebetterthanNaOH. Keywords:rubberconcrete;rubberpretreatment;mechanicalproperties;micromorphology 随着我国汽车工业的快速发展，汽车总数的急剧增多，废旧汽车轮胎的处理成为人们日 益关注的课题。直接焚烧、填埋废旧汽车轮胎会造成严重的环境污染，因此将其回收利用已 成为处理废旧轮胎的重要途径。目前，废旧轮胎橡胶的回收利用主要包括：旧橡胶翻新，生 [1] 产再生胶和生产胶粉等三种方式，但这些方式总体利用率比较有限 。据报道我国每年产生 [2] 的废旧橡胶近5000千吨，回收利用率仅在50%左右 ，如何能高效利用废旧橡胶是当前亟 待解决的环境问题。 已经有研究指出在水泥基材料中加入胶粉是一种新的处理废旧橡胶的途径，橡胶集料的 [3~5] 掺入也能起到改善混凝土脆性，起到减震、隔音和保温等作用 。但掺入橡胶会导致混凝 [6~7] 土强度下降的问题 。对于这强度下降的现象的一个解释是：橡胶与水泥浆体的粘结能力 [8~9] 差，因为憎水性的橡胶集料与水泥石之间的粘接为二者的薄弱环节 。为改善橡胶混凝土 的硬化性能，常对橡胶集料进行预处理，常用的预处理方式包括，NaOH溶液处理，偶联剂 处理及胶乳处理等[10~14]，其目的均在提高橡胶集料与水泥石基体之间的粘结。 本文主要利用酸性KMnO 的强氧化性，研究KMnO 溶液预处理 NaOH溶液预处理