自愈合 混凝土 论文.doc

混凝土裂缝自愈合性能的研究及进展 摘要: 混凝土结构因为开裂而失效的事故展展发生, 这不仅给国家、人民带来了巨大的经济损失, 而且还严重威胁着人们的人身安全. 所谓自愈合是指当混凝土结构开裂其本身会自动修复裂缝。本文阐述了自修复机理及其混凝土裂缝自愈合技术路线，包括对混凝土天然愈合能力的研究，仿生自愈合的研究及在水泥基中掺入特殊材料实现自愈合的研究，分析讨论了此领域尚存在的问题及今后的研究方向。 关键词：混凝土；裂缝；自修复；自愈合； Study and progress of crack self-healing of concret Abstract: Cracks in concert are inevitable and are one of the inherent weaknesses of concert ,which bring huge economic losses to the country people and threats to personal safety seriously .Self-healing of concrete means concrete will repair itself once the concrete structure cracking.The technology and mechanism of self- repairing for concrete are discussed in this paper，including studies of concrete’s natural repairing ability,studies of bionic self-healing concrete and studies of self-healing by add special material into cement. And the existing problems and future research directions in the field are pointed out. Key words： concert； crack;self- repairing;self-healing； 1、 引 言 混凝土作为目前用量最大的一种建筑材料, 其最大的缺点就是在材料制备过程以及服役期间，在周围环境的影响下极易在材料内部产生微裂纹而出现局部损伤。混凝土的裂缝是不可避免的，其微观裂缝是本身物理力学性质决定的。但是，若不能及时修复，不仅会影响材料的正常使用，而且可能由此诱发宏观裂缝并出现脆性断裂。形成混凝土裂缝的原因很多，大量调查研究表明，混凝土中裂缝的产生主要是由变形(包括结构因温度和湿度变化、收缩、膨胀、不均匀沉陷等原因)及外荷载(动、静荷载)所产生的应力引起的。长期以来，混凝土的裂缝一直是国内外学术界和工程界所研究的一个重要课题，发表了大量的有关混凝土裂缝成因、评估与修补的文章，并取得了许多有价值的成果[1，2]。混凝土裂缝自修复是指混凝土在外部或内部条件的作用下，释放或生成新的物质自行封闭、愈合其裂缝。混凝土的自愈合性能可以在不影响混凝土结构尺寸和美观的条件下使混凝土的裂缝产生愈合, 从而恢复和提高混凝土的性能。 2、 混凝土的自然愈合特性 实践经验表明, 混凝土自身有对损伤自然愈合的特性, 即开裂后的混凝土在潮湿条件下或在水中养护, 裂缝能达到一定程度的愈合。Abrams( 1925年) 是第一个发现混凝土具有自愈合现象的学者, 他注意到经混凝土抗压强度测定后的开裂试件在户外放置8 年后居然愈合了, 且其抗压强度为28 天强度的两倍多[ 3] 。后来国外也有资料记载龄期为三年的混凝土开裂愈合后, 强度百分之百恢复[ 4] 。国内也有类似研究成果, 李建林、朱子龙在混凝土缝愈合作用的试验研究中发现, 普通混凝土产生温度裂缝初期, 在一定的养护条件下能够自身愈合[ 5] 。混凝土自愈合特性以裂缝处有白色碳酸钙结晶为特征( 见图1[ 6] ) , 其包含复杂的物理及化学过程, 主要机理包括[ 6] : ( 1) 混凝土中未水化的水泥颗粒( 如C3S、C3A 等) 与渗透水作用并在裂缝处生成水泥水化产物; ( 2) 混凝土硬化体中微溶于水的水 化产物Ca( OH) 2 与渗透水及空气中的CO2 反应生成的碳酸钙在 裂缝周围结晶; ( 3) 水渗透导致混凝土 内部Ca( OH) 2 浓度 图1 混凝土裂缝愈合处碳酸钙的结晶特征[ 4] 降低, 致使与Ca( OH) 2 相平衡的水泥水化产物分解, 集附在裂缝周围; ( 4) 空气中的污染物如灰尘等沉落到渗