论文纳米阵列电极有机太阳能电池的制备.docVIP

纳米阵列电极/有机太阳能电池的制备 并用扫描电子显微镜对样品形貌进行了表征。Abstract Solar cells have broad application prospects，and the key factor to the solar cell application value is the conversion rate of its preparation materials. For ZnO and polythiophene special structure and properties,they have great application in the preparation of solar cells.This article through the detailed discussion on ZnO and polythiophene different preparation process,and the sample morphology are characterized by scanning electron microscope.Analyzes the effect on ZnO namo-rod growth situation of different precursor liquid concentration and different PH value and the effect on polythiophene conductivity of different temperature.The results shows that the higher the concentration of precursor liquid,the larger the diameter of ZnO namo-rod;Under a suitable high PH value, ZnO nano-rod will have a fast growth rate even in loose environment,so it is vary suitable for large-scale preparation of ZnO nano-rod arrays.And the higher the temperature,the lower the conductivity of polythiophene. Key words:Solar cells;ZnO;polythiophene 目 录 摘 要 Abstract 1 第一章 4 1 研究目的和意义 2 基本原理 4 2.1 纳米阵列电极的基本原理 4 2.2 太阳能电池的基本原理 6 第二章 7 1 溶胶-凝胶法 7 2 电化学沉积法 7 3 喷雾热分解法 8 4 金属有机物化学气相沉积法 8 5 脉冲激光沉积法 8 6 分子束外延法 9 7 水溶液生长法 9 8 化学浴沉积法 10 第三章 13 1 聚噻吩的制备 13 2 复合材料的制备 13 2.1 制备理论 13 2.1.1 浸润吸附理论 14 2.1.2 化学键理论 14 2.1.3 机械联结理论 14 2.2 制备方法 14 2.2.1 共混法 14 2.2.2 插层复合法 14 2.2.3 溶胶-凝胶法 14 第四章 结论 16 参考文献 致 谢 第一章 前言 研究的目的和意义 纳米电极由于具有高传质速率、低iR降、小时间常数等优良特性而得到了越来越广泛的研究和应用。纳米阵列电极的电化学性质不仅和纳米单电极的性质相关，而且还具有自身的一些特性，如可获得较纳米单电极大得多的电流强度，具有较相同几何面积的常规电极高得多的信噪比(S／N)等。这些特性使得纳米阵列电极的研究逐渐成为当今太阳能电池研究领域最活跃的前沿之一。 自从1839年贝克勒尔发现液体的光生伏特效应以来，特别是第一片硒太阳能电池发现以来，对于太阳能电池应用的研究一直强烈吸引着人们的注意力。由于太阳能电池无污染的特点，使其在很多应用方面，与常规电池相比具有无与伦比的优越性。 当电力、煤炭、石油等不可再生能源频频告急，能源问题日益成为制约国际社会经济发展的瓶颈时，越来越多的国家开始实行“阳光计划”，开发太阳能资源，寻求经济发展的新动力。欧洲一些高水平的核研究机构也开始转向可再生能源。在国际光伏市场巨大潜力的推动下，各国的太阳能电池制造业争相投入巨资，扩大生产，以争一席之地。 目前市场上大量太阳能电池平均效率约在15%上下，也就是说，这样的太阳电池只能将入射