SiO2对低密度聚乙烯摩擦性能与力学性能影响的研讨.pdfVIP

SiO 对低密度聚乙烯摩擦性能与力学性能影响的研究 2 王 茹，许文才，李东立 （北京印刷学院印刷包装材料与技术北京市重点实验室，北京 102600 ） 摘要：防粘剂可以改善聚乙烯的摩擦性能，起到爽滑的作用。为了定量的描 述 SiO2 防粘剂对聚乙烯摩擦系数的影响，在低密度聚乙烯中加入沉淀法合成的 SiO2 改善其摩擦性能，并对其摩擦与力学性能进行测试与分析。实验结果表明： SiO2 可以明显降低 LDPE 薄膜的摩擦系数；材料的力学性能没有发生太大的变 化；且SiO2 的加入提高了LDPE 薄膜的极性。 关键词：SiO2 ；LDPE ；摩擦性能；力学性能 Effects ofSiO on Tribological and Mechanical Properties of LDPE 2 Wang Ru，Xu Wencai，Li Dongli （Beijing Institute of Graphic Communication Laboratory of Printing Packaging Materials and Technology - Beijing Area Major Laboratory ，Beijing102600 ，China ） Abstract: Anti-adhesion agents can improve the tribological property of polyethylene . The properties of LDPE were modified by SiO , which was produced in 2 chemical precipitation, and the tribological and mechanical properties of LDPE were tested to quantificationally display the effect. The experiment results showed that the friction coefficient of LDPE film is reduced by adding SiO , and the polarity of LDPE 2 film is improved, while there isn’t any change about the mechanical Properties of LDPE. Key Words: SiO ; LDPE; tribological properties; mechanical properties 2 LDPE 塑料薄膜本身具有很高的摩擦系数，这使得它们在加工过程中具有自 行粘附和附着在加工器具表面的倾向，导致产品起皱而无法使用，降低生产效率 [1] 并使废料量增加 。塑料加工向自动化、高速化和高品质化的发展，要求降低塑 料的摩擦系数，以利于塑料加工。这就需要向塑料中添加高效的爽滑剂。 [2] [3] LDPE 包装薄膜中常见的爽滑剂多为油酸酰胺 与芥酸酰胺 。它们是在母 料熔融加工时加入，当聚合物开始冷却结晶时，迁移出母体，到达薄膜表面，形 成一层润滑层，从而有效地隔离附近的薄膜层，降低摩擦系数。但胺类爽滑剂的 价格较高且热稳定性一般。此外，防粘剂（开口剂）也会降低塑料薄膜的摩擦系 [4] 数,起到爽滑的作用。最常用的防粘剂是二氧化硅 。二氧化硅降低摩擦力的原 因是：SiO2 在LDPE 表面形成许多凸起，减少层与层之间的实际接触面积，从而 减少粘结力，使相对滑动较为容易。同胺类爽滑剂相比，二氧化硅价格较低，不