SolNit不锈钢强化工艺.pdf

SolNit®--一种新的不锈钢强化工艺 2012 Ipsen Inc 不锈钢的渗碳及渗氮 渗碳 1470ºF (800ºC) - 2100 °F (1150ºC): 由于碳化物Cr C 和Cr C 的形成，耐蚀性降低 23 6 7 3 渗氮900ºF (480ºC) -1650°F (900ºC): Loss of corrosion resistance due to nitride formation of type 由于氮化物 CrN- 和Cr N 的形成，也会使耐蚀性降低 2 This document contains proprietary information of Ipsen, Inc. It is submitted in confidence, and may not be reproduced or used for any other purpose or disclosed to others without written authorization from Ipsen, Inc. 避免不锈钢耐蚀性降低的热处理方法 渗氮：在 750°F (400ºC) - 840°F (450ºC): 形成N-原子聚集/ s-相 渗碳：在660°F (350ºC) - 840°F (450ºC) : 过饱和奥氏体，C-含量2 ~ 3% SolNit®-工艺：在1920ºF (1050ºC) - 2100 °F (1150ºC) : 奥氏体具有很高的氮溶解度 This document contains proprietary information of Ipsen, Inc. It is submitted in confidence, and may not be reproduced or used for any other purpose or disclosed to others without written authorization from Ipsen, Inc. 在1100°C奥氏体中溶解度的比较 ) % t h g i e W ( t n e t n o C - r C C- Content (Weight %) N- Content (Weight %) This document contains proprietary information of Ipsen, Inc. It is submitted in confidence, and may not be reproduced or used for any other purpose or disclosed to others without written authorization from Ipsen, Inc. SolNit® - 工艺控制 表面氮浓度及氮固溶深度取决于：  不锈钢中合金元素的含量  温度  氮分压 表面氮浓度与氮分压的关系为： NS ~ √ pN2 (Sieverts‘ 定律) This document contains proprietary information of Ipsen, Inc. It is submitted in confidence, and may not be reproduced or used for any oth