聚乙烯醇海藻酸钠共混与交联复合膜的制备研究.pdfVIP

C015 聚乙烯醇－海藻酸钠共混与交联复合膜的制备1 * 董永全 沈江南 张林 宋明宇 陈欢林 高从堦 （浙江大学材料与化工学院，浙江杭州310027 ） 摘 要 用溶液共混法制备了聚乙烯醇（PVA ）－海藻酸钠（SA）共混膜，通过红外光谱(FTIR)法、粘 度法对共混膜的相容性进行了测试，用扫描电镜（SEM）对 PVA-SA 共混膜结构进行了表征。用红外 光谱法研究了共混膜与马来酸酐交联的反应机理。 关键词 共混 海藻酸钠 聚乙烯醇 交联 相容性 PREPARATION OF BLEND AND CROSSLINKED COMPOSITE MEMBRANE OF POLY (VINYL ALCOHOL) AND SODIUM ALGINATE DONG Yongquan, ZHANG Lin, SHEN Jiangna n, SONG Mingyu CHEN Huanlin and GAO Congjie (College of Mater. Sci. and Chem. Eng., Zhejiang University, Hangzhou Zhejiang 310027, China ) Abstract PVA and SA blend membranes were prepared by solution methods. The compatibilities of the blend membranes were studied by FTIR and viscosity method, and the structures of membranes were characterized by SEM. The mechanism of the crosslinking reaction between blend membranes and maleic acid was studied by FTIR. Keywords blend, sodium alginate, poly(vinyl alcohol), cross-linking, compatibility 引 言 作为非离子型聚合物的聚乙烯醇(PVA)分子链结构规整,是严格的线型结构，分子链上含 有羟基,因而具有良好的亲水性,并且其化学性质稳定,机械强度高和良好的成膜性能,因而 越来越广泛的成为亲水性膜材料之一,尤其是作为薄层复合膜致密层膜材料[1] 。聚电解质分 子链上因为有许多强亲水性的基团，因而选择聚电解质做优先透水膜材料受到广泛的关注， 目前研究得较多的有聚丙烯酸、壳聚糖等，而海藻酸钠（SA ）是一种从海生的褐藻中提取 出来的阴离子聚电解质,其分子结构中含有大量的强亲水性基团：羟基和羧基，但是存在溶 解于水时，离解出来的反离子小分子容易流失造成膜的不稳定性。所以将这两种聚合物共混 可以利用各自的优点，有望制备出新一代膜材料。目前围绕聚乙烯醇和海藻酸钠共混的研究 已经有了一些文献报道。张可达[2]等用海藻酸钠与聚乙烯醇共混制膜分离乙醇水溶液,选择性 和渗透通量都获得了提高,可见将聚电解质与PVA 共混可以优化膜性能。Yeom[3]用PVA 和 * 作者简介：董永全，（1976－），男，四川盐亭人，博士研究生，研究方向为膜分离通讯联系人 基金项目：国家重点基础研究发展计划（973 计划）（2003CB615706 ） SA 共混均质膜对乙醇和异丙醇脱水，Aminabhavid[4]制备了PVA 和SA 的均质共混平板膜用 于异丙醇的研究，Kenshimiura[5]还就PVA 和 SA 共混膜的热力学和粘弹性能进行了研究。 Lee K-H [6-8]用质量比为95/5(wt. ％) PVA/SA 稀溶液涂布在聚砜支撑层上，然后在室温下用戊