铝合金焊接技术的研究现状与发展.doc

二 〇 一 二 年 四 月 摘 要 铝合金由于重量轻、比强度高、耐腐蚀性能好、无磁性、成形性好及低温性能好等特点而被广泛的应用于各种焊接结构产品中。因此提高铝合金焊接的生产率和焊接质量，减少焊接缺陷存在的高效焊接方法已成为实际生产的迫切要求。本文综述了铝合金几种先进的焊接工艺：钨极氩弧焊（TIG）、激光焊（LBW）、搅拌摩擦焊（FSW），及其焊接发放和特点，并指出在焊接中存在的问题以及未来的发展趋势。 关键词：铝合金；钨极氩弧焊（TIG）；激光焊（LBW）；搅拌摩擦焊（FSW） Abstract Aluminum alloy because of light weight, high specific strength, good corrosion resistance, no magnetism, good formability and low temperature characteristics of a good performance and has been widely used in all kinds of welding structure product. Therefore, to improve the productivity of aluminum alloy welding and welding quality, reduce welding defect in the presence of high efficient welding method has become the urgent requirements of actual production. This paper summarized several advanced welding technology of aluminum alloy: tungsten argon arc welding(TIG)， laser welding(LBW),friction stir welding(FSW),and the distribution and characteristics of welding, and points out that in the welding problems and future development trend. Key words: aluminum alloy; tungsten argon arc welding(TIG)；laser welding (LBW)；friction stir welding(FSW) 目 录 摘 要 I Abstract II 引 言 1 第一章 铝合金的焊接特点 2 1.1. 铝合金的焊接特点 2 1.2. 铝合金焊接的几大难点 2 第二章 铝合金的焊接工艺 3 2.1. 钨极氩弧焊（TIG） 3 2.1.1. TIG焊的基本原理 3 2.1.2. TIG焊的特点 3 2.1.3. 铝合金的TIG焊 4 2.2. 激光焊（LBW） 6 2.2.1. 激光焊的基本原理 6 2.2.2. 铝合金激光焊的特点 6 2.2.3. 铝合金的激光一电弧复合焊 6 2.3. 搅拌摩擦焊（FSW） 7 2.3.1. FSW焊的基本原理 7 2.3.2. FSW焊的特点 7 2.3.3. 铝合金的FSW焊 8 总 结 10 参考文献 11 谢 辞 13 引 言 铝是工业上应用最广泛的重要有色金属之一。铝及铝合金具有密度小、重量轻，热容量大、熔化潜热高、强度高及良好的耐蚀性、导电性、导热性，以及在低温下能保持良好的力学性能等优点。铝及铝合金在航空航天、国防、汽车、电工、化工、交通运输等行业中被广泛应用，这也极大地推动了铝合金焊接技术的发展，因此，提高铝合金焊接的生产率和焊接质量，减少焊接缺陷存在的高效焊接方法已成为实际生产的迫切要求。 铝合金其主要成分是铝，而铝的密度较低，熔点低热传导性能好，热膨胀系数大，同时其具有很强的化学活泼性，易氧化，且氧化物的熔点很高。在与其他组元形成合金后依然保持这些特性，因此铝合金在焊接过程中存在着一系列的问题，如：氧化、裂纹、气孔、接头力学性能下降、热影响区变宽等。为了提高铝合金焊接接头的质量，近年来涌现出了许多新的铝合金焊接方法，如：钨极氩弧焊（TIG）、激光焊（LBW）、电子束焊（EBW）、搅拌摩擦焊（FSW）等。 本文介绍了铝合金的几种先进的焊接工艺，几种工艺均具有优越性，并针对铝合金的焊接困难提出了有效的解决办法。 第一章 铝合金的焊接特点 铝合金的焊接特点 铝合金重量轻、比强度高、耐腐蚀性能好、无磁性、成形性好及低温性能好等特点而被广泛的应用于各种焊接结构产品中。 铝合金